通过选择络合剂、缓冲剂及采用方波脉冲电流和优化电镀工艺,在酸性镀液中实现了Cr-Pd共镀,并在不锈钢表面制备出均匀致密且与基体结合良好的Cr-Pd合金镀层.通过改变镀液中铬盐和钯盐的相对含量,可以大范围改变镀层成分.Cr-Pd合金镀层可显著提高不锈钢在高温还原性腐蚀介质中的耐蚀性,在沸腾的20%(质量分数)H2SO4溶液中,Cr-Pd合金镀层使316L不锈钢的腐蚀速率降低了4个数量级以上.镀层中的Cr和Pd对致钝具有协同促进作用,当镀层中含有2.5%Pd(质量分数)时即具有明显的促进钝化效果,含33.3%Pd镀层对不锈钢的保护效果与纯Pd镀层相当.
参考文献
| [1] | Tang J L,Zuo Y.Corros Sci,2008; 50:2873 |
| [2] | Zuo Y,Tang J L,Fan C Z,Tang Y M,Xiong J P.Thin Solid Films,2008; 516:7565 |
| [3] | Tang J L,Zuo Y,Tang Y M,Xiong J P.Surf Coat Technol,2010; 204:1637 |
| [4] | Gao X,Tang J L,Zuo Y,Tang Y M,Xiong J P.Corros Sci,2009; 51:1822 |
| [5] | Samaik K M,Palrecha M M,Dhaneshwar R G.J Electrochem Soc,1989; 136:283 |
| [6] | Hsieh A K,Ee Y H.Met Finish,1993; 91:53 |
| [7] | Zeng Z,Liang A,Zhang J.Electrochim Acta,2008; 53:7344 |
| [8] | Abys J A.US Pat,6346222,2002 |
| [9] | Li B,Lin A,Wu X,Zhang Y,Gan F.J Alloys Compd,2008; 453:93 |
| [10] | Yang F Z,Xu S K,Yao S B,Chen B Y,Zheng X Q,Zhong X H,Zhou S M.Electrochemistry,1997; 3(1):107(杨防祖,许书楷,姚士冰,陈秉彝,郑雪清,钟晓慧,周绍民.电化学,1997;3(1):107) |
| [11] | Lü W,Zhang Y X.J Fujian Norm Univ (Nat Sci),2002; 18(1):51(吕玮,张永祥.福建师范大学学报(自然科学版),2002;18(1):51) |
| [12] | Guan S,Zhang Q,Hu R N.Mater Prot,2000; 20(3):1(关山,张琦,胡如南.材料保护,2000;20(3):1) |
| [13] | Hou J L,Yan X J,Feng L J,Zhu J.Foundry Technol,2009; 30:1067(侯娟玲,闫小军,冯拉俊,祝捷.铸造技术,2009;30:1067) |
| [14] | Raub Ch J.Platinum Metals Rev,1982; 26:158 |
| [15] | Hamm D,Olsson C A,Landolt D.Corros Sci,2002; 44:1009 |
| [16] | Hernias A A,Nakayama M,Ogura K.Electrochim Acta,2005; 50:2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%