通过单轴拉伸实验并结合原位电阻测量法系统研究了恒定调制比下调制波长(λ=10-250 nm)对聚酰亚胺基体上Cu/Nb纳米金属多层膜延性和断裂韧性的影响.微观分析表明,Cu/Nb的调制结构清晰,不存在明显的互混现象.实验结果表明,随着调制波长的减小,多层膜的延性和断裂韧性均呈现非单调演变趋势,在调制波长为50 nm左右出现峰值.这是由于随着层厚的变化,脆性Nb层内起始微裂纹扩展能力和延性Cu层抑制裂纹扩展能力这两个因素之间的相互竞争关系变化引起的.采用断裂力学理论对这种竞争关系及其引起的延性和断裂韧性非单调变化趋势进行了定性分析.
参考文献
| [1] | Spearing S M.Acta Mater,2000; 48:179 |
| [2] | Suo Z G,Vlassak J,Wagner S.China Particuology,2005; 3:321 |
| [3] | Bakonyi I,Péter L.Prog Mater Sci,2010; 55(3):107 |
| [4] | Was G S,Foecke T.Thin Solid Films,1996; 286:1 |
| [5] | Misra A,Krug H.Adv Eng Mater,2001; 3(4):217 |
| [6] | Misra A,Hirth J P,Hoagland R G.Acta Mater,2005; 53:4817 |
| [7] | Phillips M A,Clemens B M,Nix W D.Acta Mater,2003; 51:3171 |
| [8] | Huang H B,Spaepen F.Acta Mater,2000; 48:3261 |
| [9] | Mara N A,Bhattacharyya D,Hoagland R G,Misra A.Scr Mater,2008; 58:874 |
| [10] | Niu R M,Liu G,Wang C,Zhang G,Ding X D.Appl Phys Lett,2007; 90:161907 |
| [11] | Li Y P,Tan J,Zhang G P.Scr Mater,2008; 59:1226 |
| [12] | Li Y P,Zhang G P.Acta Mater,2010; 58:3877 |
| [13] | Zhu X F,Li Y P,Zhang G P,Tan J,Liu Y.Appl Phys Lett,2008; 92:161905 |
| [14] | Yu D Y W,Spaepen F.J Appl Phys,2004; 95:2991 |
| [15] | Zhang J Y,Zhang X,Liu G,Zhang G J,Sun J.Scr Mater,2010; 63:101 |
| [16] | Hertzberg R W.Deformation and Fracture Mechanics of Engineering Materials.New York:John Wiley,1989:15 |
| [17] | Dundurs J,Bogy D B.J Appl Mech,1969; 36:650 |
| [18] | Jr Beuth J L.Int J Solids Struct,1992; 29:1657 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%