采用激光熔覆结合熔覆层激光快速重熔工艺,在45钢表面制备了成形良好、稀释率低的Cu-Mn合金涂层,涂层微观组织为细小的树枝晶,随着激光重熔速度的提高,二次枝晶间距统计平均值从3.1μm减小为1.6μm.动电位扫描测试表明,对于不同的电解液,Cu-Mn合金表现出选择性溶解特性.对合金涂层在HCI和KNO3溶液中进行电解腐蚀脱合金后,分别成功制备了纳米多孔结构的Cu涂层和Mn涂层.纳米多孔Cu孔径尺寸为30-50 am,而纳米多孔Mn的微观形貌为类似于"丝瓜筋"的网状结构,粗糙度系数高达900.
参考文献
| [1] | Li H X,Zhao Q F,Wan Y,Dai W L,Qiao M H.J Cotal,2006:244:251 |
| [2] | Pugh D,Dursun A,Corcoran S.J Mater Res,2003;18:216 |
| [3] | Thomas K.Catal Today,2007;120:389 |
| [4] | Ding Y,Chen M W,Erlebacher J.J Am Chem Soc,2004;126:6876 |
| [5] | Uchic M D,Dimiduk D M,Florando J N,Nix W D.Science,2004;305:986 |
| [6] | Smith A J.Ann Rev Mater Res,2005;35:127 |
| [7] | Min U S,Li J C M.J Mater Res,1994;9:2878 |
| [8] | Li S,Chien C L,Searson P C.Chem Mater,2004;16:3125 |
| [9] | Chang J K,Hsu S H,Sun I W,Tsai W T.J Phys Chem,2008;112C:1371 |
| [10] | Hayes J R,Hodge A M,Biener J,Hamza A V.J Mater Res,2006;21:2611 |
| [11] | Chen L Y,Yu J S,Fujita T,Chen M W.Adv Funct Mater,2009;19:1 |
| [12] | Lu H B,Li Y,Wang F H.Scr Mater,2007;56:165 |
| [13] | Kan Y D,Ma M X,Liu W J,Zhong M L,Gu Y,Dong C S,Zhang H J.Appl Laser,2008;28:455(阚义德,马明星,刘文今,钟敏霖,谷雨,董长胜,张红军.应用激光,2008;28:455) |
| [14] | Jia F L,Yu C F.Ai Z H,Zhang L Z.Chem Mater,2007;19:3648 |
| [15] | Liu H T,He P,Li Z Y,Li J H.Nanotechnology,2006;17:2167 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%