通过常规金属型铸造工艺制备准晶相增强的Mg-8Zn-4Al(ZA84)和Mg-8Zn-4Al-0.5Y(ZAY8405)合金,采用Gleeble-1500热模拟试验机在温度230℃和应变速率0.0015-1.5 s-1的条件下,对准晶增强的Mg-Zn-Al-(Y)合金的热压缩变形行为进行了研究.结果表明:ZA84和ZAY8405合金铸态组织主要由二十面体准晶和α-Mg所组成,Y的加入可进一步细化凝固过程中形成的准晶相；Mg-Zn-Al-(Y)合金热变形过程中合金发生典型的动态再结晶,流变应力随应变速率增大而增大,并可通过幂指数模型进行描述,应变速率变化对ZAY8405合金流变应力的影响更大；热变形过程中,准晶可促进Mg-Zn-Al-(Y)合金的动态再结晶,ZAY8405合金中弥散分布的细小准晶以及Y的加入更有利于孪生和动态再结晶的发生.
参考文献
| [1] | Decker R F.Adv Mater Processes,1998; 154(3):31 |
| [2] | Liu Q.Acta Metall Sin,2010; 46:1458(刘庆.金属学报,2010; 46:1458) |
| [3] | Lu Y Z,Wang Q D,Ding W J.Mater Lett,2000; 44:265 |
| [4] | Mukai T,Yamanoi M,Watanabe H,Higashi K.Scr Mater,2001; 45:89 |
| [5] | Kim W J,Hong S I,Kim Y S.Acta Mater,2003; 51:3293 |
| [6] | Yang X Y,Zhang L.Acta Metall Sin,2009; 45:1303(杨续跃,张雷.金属学报,2009; 45:1303) |
| [7] | Jin Q L,Shim S Y,Lim S G.Scr Mater,2006; 55:843 |
| [8] | Shechtman D,Blech I,Gratias D,Cahn J W.Phys Rev Lett,1984; 53:1951 |
| [9] | Yuan G Y,Liu Y,Ding W J.Mater Sci Eng,2008; A474:348 |
| [10] | Liu Y,Yuan G Y,Lu C.J Mater Sci,2008; 43:5527 |
| [11] | Somekawa H,Singh A,Mukai T.Adv Eng Mater,2009;11:782 |
| [12] | Yuan G Y,Amiya K,Kato H,Inoue A.J Mater Res,2008;19:1531 |
| [13] | Elser V.Phys Rev,1985; 32B:4892 |
| [14] | Bourgeois L,Mendis C L,Muddle B C.Philos Mag Lett,2001; 81:709 |
| [15] | Vogel M,Kraft O,Behm G.Scr Mater,2001; 45:517 |
| [16] | Galiyev A,Kaibyshev R,Gottstein G.Acta Mater,2001;49:1199 |
| [17] | Agnew S R,Yoo M H,Tome C N.Acta Mater,2001; 49:4277 |
| [18] | Li Z J,Jin Q L,Jiang Y H,Zhou R.Acta Metall Sin,2009;45:924(李再久,金青林,蒋业华,周荣.金属学报,2009; 45:924) |
| [19] | Bae D H,Kim S H,Kim D H,Kim W T.Acta Mater,2002; 50:2343 |
| [20] | Singh A,Watanabe M,Kato A,Tsai A P.Sci Technol Adv Mater,2005; 6:895 |
| [21] | Lee J Y,Lim H K,Kim D H,Kim W T,Kim D H.Mater Sci Eng,2008; A491:349 |
| [22] | Hu G X,Cai X.Fundamental of Material Science.Shanghai:Shanghai Jiao Tong University Press,2004:193(胡赓祥,蔡珣.材料科学基础.上海:上海交通大学出版社,2004:193) |
| [23] | Yu K,Shi T,Wang R C,Li W X,Wang X Y,Cai Z Y.J Cent South Univ (Sci Technol),2008; 39:216(余琨,史褆,王日初,黎文献,王晓艳,蔡志勇.中南大学学报(自然科学版),2008; 39:216) |
| [24] | Poirier J P,translated by Guan D L.The Plastic Deformation of Crystals at High Temperature.Dalian:Dalian University of Science and Technology Press,1989:25(Poirier J P著,关德林译.晶体的高温塑性变形.大连:大连理工大学出版社,1989:25) |
| [25] | Takuda H,Fujimoto H,Hatta N.J Mater Process Technol,1998; 80-81:513 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%