研究了温度为150℃,电流密度为5.0×103 A/cm2的条件下电迁移对Ni/Sn3.0Ag0.5Cu/Cu焊点界面反应的影响.回流焊后在Sn3.0Ag0.5Cu/Ni和Sn3.0Ag0.5Cu/Cu的界面上均形成了(Cu,Ni)6Sn5型化合物.时效过程中界面化合物随时效时间增加而增厚,时效800 h后两端的化合物并没有发生转变,仍为(Cu,Ni)6Sn5型.电流方向对Cu基板的消耗起着决定作用.当电子从基板端流向芯片端时,电流导致基板端Cu焊盘发生局部快速溶解,并导致裂纹在Sn3.0Ag0.5Cu/(Cu,Ni)6Sn5界面产生,溶解到钎料中的Cu原子在钎料中沿着电子运动的方向向阳极扩散,并与钎料中的Sn原子发生反应生成大量的Cu6Sn5化合物颗粒.当电子从芯片端流向基板端时,芯片端Ni UBM层没有发生明显的溶解,在靠近阳极界面处的钎料中有少量的Cu6Sn5化合物颗粒生成,电迁移800 h后焊点仍保持完好.电迁移过程中无论电子的运动方向如何,均促进了阳极界面处(Cu,Ni) 6Sn5的生长,阳极界面IMC厚度明显大于阴极界面IMC的厚度.与Ni相比,当Cu作为阴极时焊点更容易在电迁移作用下失效.
参考文献
[1] | Zeng K,Tu K N.Mater Sci Eng Rep,2002; 38(2):55 |
[2] | Chen C,Tong H M,Tu K N.Annu Rev Mater Res,2010;40:531 |
[3] | Tu K N,Gusak A M,Li M.J Appl Phys,2003; 93:1335 |
[4] | He H W,Xu G C,Guo F.Acta Metall Sin,2009; 45:744(何洪文,徐广臣,郭福.金属学报,2009:45:744) |
[5] | Gan H,Tu K N.J Appl Phys,2005; 97:063514 |
[6] | Yang Q L,Shang J K.J Electron Mater,2005; 34:1363 |
[7] | Lin Y H,Hu Y C,Tsai C M,Kao C R,Tu K N.Acta Mater,2005; 53:2029 |
[8] | Lu Y D,He X Q,En Y F,Wang X,Zhuang Z Q.Acta Metall Sin,2009; 45:178(陆裕东,何小琦,恩云飞,王歆,庄志强.金属学报,2009; 45:178) |
[9] | Zhang L Y,Ou S Q,Huang J,Tu K N,Gee S,Nguyen L.Appl Phys Lett,2006; 88:012106 |
[10] | Hung Y M,Chen C M.J Electron Mater,2008; 37:887 |
[11] | Hu Y C,Lin Y H,Kao C R,Tu K N.J Mater Res,2003;18:2544 |
[12] | Chen L D,Huang M L,Zhou S M.J Alloys Compd,2010;504:535 |
[13] | Zhang X F,Guo J D,Shang J K.J Mater Res,2008; 23:3370 |
[14] | Zhang F,Li M,Chum C C,Tung C H.J Mater Res,2003;18:1333 |
[15] | Wang S J,Liu C Y.J Electron Mater,2003; 32:1303 |
[16] | Wang S J,Liu C Y.J Electron Mater,2006; 35:1955 |
[17] | Chen H T,Wang C Q,Yan C,Li M Y,Huang Y.J Electron Mater,2007; 36:26 |
[18] | Hong K K,Ryu J B,Park C Y,Huh J Y.J Electron Mater,2008; 37:61 |
[19] | Chang C W,Yang S C,Tu C T,Kao C R.J Electron Mater,2007; 36:1455 |
[20] | Zhang X F,Guo J D,Shang J K.J Electron Mater,2009;38:425 |
[21] | Wu W H,Chung H L,Chen C N,Ho G E.J Electron Mater,2009; 38:2563 |
[22] | Lee T Y,Tu K N,Frear D R.J Appl Phys,2001; 90:4502 |
[23] | Harcuba P,Janecek M.J Electron Mater,2010; 39:2553 |
[24] | Taai J Y,Hu Y C,Tsai C M,Kao C R.J Electron Mater,2003; 32:1203 |
[25] | Yeh E C C,Choi W J,Tu K N,Elenius P,Balkan H.Appl Phys Lett,2002; 80:580 |
[26] | Ho P S,Kwok T.Rep Prog Phys,1989; 52:301 |
[27] | Huang J R,Tsai C M,Lin Y W,Kao C R.J Mater Res,2008; 23:250 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%