采用SEM,TEM和物理化学相分析等方法对铁素体基Ti-Mo微合金钢在2种不同轧制工艺下的析出相分布和粒度进行了观察和统计,结合热力学和动力学计算研究了γ相区变形过程中形变储能对诱导析出的影响,分析了γ相区形变诱导析出量对后续γ→α相变以及相变后α相基体中继续析出时析出相的临界晶核尺寸、相对形核率和相对沉淀开始时间的影响.结果表明,在总变形量相同的情况下,与γ相再结晶区和未再结晶区两阶段轧制相比较,采用γ相再结晶区单阶段轧制更有利于获得析出量大,尺度分布均匀的个位纳米级碳氮化物,这类碳氮化物占析出物总量的75％(质量分数).
参考文献
| [1] | Funakawa Y,Shiozaki T,Tomita K,Yamamoto T,Maeda E.ISIJ Int,2004; 44:1945 |
| [2] | Chen C Y,Yen H W,Kao F H,Li W C,Huang C Y,Yang J R,Wang S H.Mater Sci Eng,2009; A499:162 |
| [3] | Funakawa Y,Seto K.Mater Sci Forum,2007; 539-543:4813 |
| [4] | Duan X G,Cai Q W,Wu H B.Acta Metall Sin,2011; 47:251 (段修刚,蔡庆伍,武会宾.金属学报,2011:47:251) |
| [5] | Jung J G,Park J S,Kim J,Lee Y K.Mater Sci Eng,2011;A528:5529 |
| [6] | Craven A J,He K,Garvie L A J,Baker T N.Acta Mater,2000; 48:3857 |
| [7] | Niu T,Kang Y L,Gu H W,Yin Y Q,Qiao M L.J Iron Steel Res Int,2010; 17:73 |
| [8] | Hong S G,Kang K B,Park C G.Scr Mater,2002; 46:163 |
| [9] | Hu B H.Master Dissertation,University of Science and Technology Beijing,2012 (胡彬浩.北京科技大学硕士学位论文,2012) |
| [10] | Okamoto R,Borgenstam A,Agren J.Acta Mater,2010;58:4783 |
| [11] | Okamoto R,Agren J.Acta Mater,2010; 58:4791 |
| [12] | Duan X G,Cai Q W,Wu H B,Tang D.J Univ Sci Technol Beijing,2012; 34:644 (段修刚,蔡庆伍,武会宾,唐荻.北京科技大学学报,2012:34:644) |
| [13] | Pickering F B.Physical Metallurgy and the Design of Steels.London:Applied Science Publishing Ltd,1978:63 |
| [14] | Duan X G.PhD Thesis,University of Science and Technology Beijing,2012 (段修刚.北京科技大学博士学位论文,2012) |
| [15] | Cao J C.PhD Thesis,Kunming University of Science and Technology,2006 (曹建春.昆明理工大学博士学位论文,2006) |
| [16] | Yong Q L.Secondary Phase in Steel.Beijing:Metallurgical Industry Press,2006:1 (雍岐龙.钢铁材料中的第二相.北京:冶金工业出版社,2006:1) |
| [17] | Zhang L Z,Zhao X M,Wu D,Xu Y B.JIron Steel Res,2006; 18(4):41 (张良哲,赵宪明,吴迪,许云波.钢铁研究学报,2006; 18(4):41) |
| [18] | Zhang L,Xue C X,Yang W Y,Sun Z Q.Acta Metall Sin,2007; 43:791 (张玲,薛春霞,杨王玥,孙祖庆.金属学报,2007; 43:791) |
| [19] | Yong Q L,Chen M X,Pei H Z,Pan L,Zhou X L,Yang T W,Zhong W,Hao J Y.J Iron Steel Res,2006; 18(3):30 (雍岐龙,陈明昕,裴和中,潘俐,周晓玲,杨天武,钟卫,郝建英.钢铁研究学报,2006:18(3):30) |
| [20] | Funakawa Y.Mater Sci Forum,2012; 706-709:2096 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%