采用真空非自耗电弧熔炼方法制备了4种不同Mo含量的Zr-0.4Fe-1.0Cr-xMo(x=0,0.2,0.4,0.6,质量分数,%)合金材料,研究了其在500℃,10.3 MPa过热水蒸汽中的耐腐蚀性能以及添加Mo对合金耐腐蚀性能的影响.结果表明,Zr-0.4Fe-1.0Cr-xMo合金中含有大量细小的第二相粒子,其腐蚀速率远远低于Zr-4,N18和M5合金.Mo的添加促进了氧化膜生长过程中的演变,降低了耐腐蚀性能.不含Mo合金的氧化膜生长动力学在整个腐蚀周期(2000 h)内一直保持近似立方规律,而含Mo合金的氧化膜生长动力学在500-1000 h内由近似立方规律向直线规律转变.
参考文献
[1] | Mardon J P,Chavquet D,Senevat J.In:Sabol G P,Moan G D eds.,Zirconium in the Nuclear Industry:12th International Symposium,ASTM STP 1354,West Conshonocken:ASTM International,2000:505 |
[2] | Comstock R J,Schoenberger G,Sabol G P.In:Bradley E R,Sabol G P eds.,Zirconium in the Nuclear Industry:11th International Symposium,ASTM STP 1295,West Conshonocken:ASTM International,1996:710 |
[3] | Garde A.In:Limbak M,Bareris P eds.,Zirconium in the Nuclear Industry,16th International Symposium,ASTM STP 1529,West Conshonocken:ASTM International,2010:9 |
[4] | Pahutova M,Kucharova K,Cadek J.Mater Sci Eng,1977;27:239 |
[5] | Pahutova M,Cadek J.Mater Sci Eng,2004; 33:1362 |
[6] | Chun Y B,Hwang S K,Kim M H,Kwun S I,Kim Y S.J Nucl Mater,1999; 265:28 |
[7] | Isobe T,Matsuo Y.In:Eucken C M,Garde A M eds.,Zirconium in the Nuclear Industry,9th International Symposium,ASTM STP 1132,West Conshonocken:ASTM International,1991:346 |
[8] | Chun Y B,Hwang S K,Kwun S I,Kim M H.Scr Mater,1999; 40:1165 |
[9] | Lee J H,Hwang S K,Yasuda K,Kinoshita C.J Nucl Mater,2001; 289:334 |
[10] | Moon J R,Lees D G.Corros Sci,1970; 10:85 |
[11] | Moon J R,Evans E W.Corros Sci,1969; 9:323 |
[12] | Lee J H,Hwang S K.J Nucl Mater,2003; 321:238 |
[13] | George P S,Robert J C,Umesh P N.In:Sabol G P,Moan G D eds.,Zirconium in the Nuclear Industry:12th International Syposium,ASTM STP 1354,West Conshonocken:ASTM International,2000:525 |
[14] | Motta A T,Aylin Y,Marcelo J G,Comstock R J,Was G S,Busby J T,Gartner E,Peng Q J,Jeong Y H,Park J Y.J Nulc Mater,2007; 371:61 |
[15] | Wang J,Long C S,Xiong J,Miao Z,Fang H Y,Huang Z H,Ying S H.Nucl Power Eng,2009; 30:58(王均,龙冲生,熊计,苗志,范洪远,黄照华,应诗浩.核动力工程,2009; 30:58) |
[16] | Yao M Y,Wang J H,Peng J C,Zhou B X,Li Q.In:Limbak M,Bareris Peds.,Zirconium in the Nuclear Industry,16th International Symposium,ASTM STP 1529,West Conshonocken:ASTM International,2011:466 |
[17] | Li S L,Yao M Y,Zhang X,Geng J Q,Peng J C,Zhou B X.Acta Metall Sin,2011; 47:163(李士炉,姚美意,张欣,耿建桥,彭建超,周邦新.金属学报,2011:47:163) |
[18] | Yao M Y,Li S L,Zhang X,Peng J C,Zhou B X,Zhao X S,Shen J Y.Acta Metall Sin,2011; 47:865(姚美意,李士炉,张欣,彭建超,周邦新,赵旭山,沈剑韵.金属学报,2011:47:865) |
[19] | Barberis P,Merle-Mejean T,Quintard P.J Nulc Mater,1997; 246:232 |
[20] | Barberis P,Corroleur T G,Guinbretiere R,Merle M T,Mirgorodsky A,Quintard P.J Nulc Mater,2001; 288:241 |
[21] | Godlewski J,Gross J P,Lambertin M,Wadier J F,Weidinger H.In:Eucken C M,Gaxde A M eds.,Zirconium in the Nuclear Industry,9th International Symposium,ASTM STP 1132,West Conshonocken:ASTM International,1991:416 |
[22] | Liu J Z ed.Nuclear Structural Materials.Beijing:Chemical Industry Press,2007:27(刘建章 主编.核结构材料.北京:化学工业出版社,2007:27) |
[23] | Li Q,Zhou B X,Yao M Y,Liu W Q,Chu Y L.Rare Met Mater Eng,2007; 36:1358(李强,周邦新,姚美意,刘文庆,褚于良.稀有金属材料与工程,2007; 36:1358) |
[24] | IAEA-TECDOC-996.Waterside Corrosion of Zirconium Alloys in Nuclear Power Plants.Vienna,IAEA,1998:9 |
[25] | Jong H B,Yong H J.J Nulc Mater,2000; 280:235 |
[26] | Zhou B X,Li Q,Yao M Y,Liu W Q,Chu Y L.In:Kamenzind B,Limback Meds.,Zirconium in the Nuclear Industry:15th International Symposium,ASTM STP 1505,West Conshonocken:ASTM International,2009:360 |
[27] | Zhou B X,Li Q,Liu W Q,Yao M Y,Chu Y L.Rare Met Mater Eng,2006; 35:1009(周邦新,李强,刘文庆,姚美意,褚于良.稀有金属材料与工程,2006; 35:1009) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%