通过组织形态观察和XRD分析,研究了热处理对GH4169G合金相组成和分布规律的影响.结果表明,在实验条件下,合金的组织结构由γ基体、粒状γ’相、圆盘状γ"相和δ相组成,且各相之间保持共格界面,其中,直接时效处理ITF-DA-GH4169G合金由少量γ'相、大量γ"相和γ基体组成,而长期时效处理ITF-DA-LTA-GH4169G合金由少量γ'相、大量γ"相和γ相及针状δ相组成.时效期间,随着合金中Nb原子扩散进入γ'相,使γ'相(001)面的Nb和Ni原子沿1/2<110>方向迁移,L12结构的γ'-Ni3Al相可转变成DO22结构的γ"-Ni3Nb相.随时效时间延长,γ"相长大,γ"相单胞中的平行六面体沿特定晶面发生1/6<112>位移,促使γ"相转变成DOa结构的δ-Ni3Nb.其中,γ"相中的a,b轴与γ基体和γ'相保持共格界面,可使其沿c轴生长成为圆盘状形态；而δ-Ni3Nb相的{200}δ晶面与γ基体的{111}γ晶面保持共格界面,是促使δ相沿(100)晶面生长成为针状的主要原因.
参考文献
| [1] | Chen W,Chaturvedi M C.Mater Sci Eng,1994; A183:81 |
| [2] | Wang Y,Lin L,Shao W Z,Zhen L,Zhang X M.Trans Mater Heat Treatment,2007; 28(suppl):176(王岩,林琳,邵文柱,甄良,张新梅.材料热处理学报,2007;28(增刊):176 |
| [3] | Medeiros S C,Prasad Y V R K,Frazier W G,Srinivasan R.Mater Sci Eng,2003; A193:198 |
| [4] | Rao G A,Kymar M,Srinivas M,Sarma D S.Mater Sci Eng,2003; A355:114 |
| [5] | Xie X S,Dong J X,Fu S H,Zhang M C.Acta Metall Sin,2010; 46:1289(谢锡善,董建新,付书红,张麦仓.金属学报,2010; 46:1289) |
| [6] | Zhang M Y,Wang Y X,Chen Z,Dong W P,Lai Q B,Zhang L P.Rare Met Mater Eng,2009; 38:962(张明义,王永欣,陈铮,董卫平,来庆波,张利鹏.稀有金属材料与工程,2009; 38:962) |
| [7] | Mukherji D,Gilles R,Barbier B,Del D G.Scr Mater,2003; 48:333 |
| [8] | Ding R G,Rong T S,Knott J F.Mater Sci Technol,2006;21:85 |
| [9] | Zhang M Y,Chen Z,Wang Y X,Lu Y L,Zhang J,Fan X L.Acta Metall Sin,2009; 45:930(张明义,陈铮,王永欣,卢艳丽,张静,范晓丽.金属学报,2009; 45:930) |
| [10] | Briant C L.Metall Trans,1988; 19A:137 |
| [11] | Seah M P.Acta Metall,1980; 28:955 |
| [12] | Liu D,Luo Z J.Rare Met,2005; 29:152(刘东,罗子健.稀有金属,2005; 29:152) |
| [13] | Xie X S,Dong J X,Fu S H,Zhang M C.Acta Metall Sin,2010; 46:1289(谢锡善,董建新,付书红,张麦仓.金属学报,2010; 46:1289) |
| [14] | Wang Y,Shao W Z,Zhen L.Chin J Nonferrous Met,2011;21:341(王岩,邵文柱,甄良.中国有色金属学报,2011; 21:341) |
| [15] | Hu Z Q,Sun W R,Guo S R,Lu D Z.Chin J Nonferrous Met,2001; 11:947(胡壮麒,孙文儒,郭守仁,卢德忠.中国有色金属学报,2001; 11:947) |
| [16] | Kirman I,Warrington D H.Metall Trans,1970; 1:2667 |
| [17] | Chaturvedi M C,Han Y F.Met Sci,1983; 17:145 |
| [18] | V anderschaeve G,Escaig B.Philos Mag,1983; 48A:265 |
| [19] | Yamakov V,Wolf D,Phillpot S R,Mukherjee A,Gleiter H.Nat Mater,2004; 3:43 |
| [20] | Van Swygenhoven H,Derlet P M,Froseth A.Nat Mater,2004; 3:399 |
| [21] | Liao X Z,Zhou F,Lavernia E J,He D W,Zhu Y T.Appl Phys Lett,2003; 83:5062 |
| [22] | Wang J,Huang H C.Appl Phys Lett,2004; 85:5983 |
| [23] | Zhen L,Xu T D,Deng Q,Si H,Dong J X.Acta Metall Sin,2007; 43:893(郑磊,徐庭栋,邓群,司红,董建新.金属学报,2007; 43:893) |
| [24] | Song H W,Guo S R,Lu D z,Xu Y,Wang Y L,Hu Z Q.Chin J Mater Res,2000; 14:183(宋洪伟,郭守仁,卢德忠,徐岩,王玉兰,胡壮麒.材料研究学报,2000; 14:183) |
| [25] | Ling B,Zhong B W,Yang Y R,Liang X F,Shen B.J Aeronaut Mater,1994; 1:1(凌斌,钟炳文,杨玉荣,梁学锋,沈飚.航空材料学报,1994;1:1) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%