采用恒载荷延迟断裂、氢热分析(TDS)等实验方法,研究了一种低碳Mn-B系超高强度热成形钢板在热成形态和常规淬火回火态的氢致延迟断裂行为.结果表明,经热成形后,试样缺口临界应力和断裂寿命均高于常规淬火态,并达到常规淬火态+100℃回火试样的水平.热成形试样经200℃回火处理后,具有更高的缺口临界应力和断裂寿命.SEM观察发现,在外加应力和腐蚀液的作用下,热成形试样裂纹源区的断裂机制由常规淬火试样的沿晶+穿晶准解理的混合断裂变为穿晶准解理+少量沿晶的混合断裂.TDS实验结果表明,在临界应力作用下,在腐蚀液中加载100 h后,试样中的H含量均明显提高.由于试样在热成形过程中发生较高程度的自回火,导致经应力腐蚀后,试样在断裂过程中能承受的H量高于淬火态试样和常规淬火态+100℃回火试样,使试样具有更高的延迟断裂抗力.因此,经热成形处理后,试样具有良好的耐延迟断裂性能,且回火处理能使试样的耐延迟断裂性能得到进一步提高.
参考文献
| [1] | Nicolas Y.Thyssen Krupp Techforum,2005; (7):40 |
| [2] | Gciger M,Merklein M,Hoff C.Adv Mater Res,2005; 6 8:795 |
| [3] | Altan T.Stamping J,2006; (12):40 |
| [4] | Sato M,Utsumi Y,Watanabe K.Kobelco Technol Rev,2008; 28:13 |
| [5] | Karbasian H,Tekkaya A E.J Mater Process Technol,2010; 210:2103 |
| [6] | Lee S J,Ronevich J A,Krauss G,Matlock D K.ISIJ Int,2010; 50:294 |
| [7] | Hein P,Wilsius J.Steel Res Int,2008; 79(2):85 |
| [8] | Suehiro M,Maki J,Kusumi K,Ogami M,Miyakoshi T.Nippon Steel Tech Rep,2003; (88):16 |
| [9] | Chu W Y.Hydrogen Damage and Delayed Fracture.Beijing:Metallurgy Industry Press,2000:149(褚武扬.氢损伤与滞后断裂.北京:冶金工业出版社,2000:149) |
| [10] | Hui W J,Weng Y Q,Dong H.High Strength FastenersSteels.Beijing:Metallurgy Industry Press,2009:32(惠卫军,翁宇庆,董瀚.高强度紧固件用钢.北京:冶金工业出版社,2009:32) |
| [11] | Hoji T,Sugimoto K,Mukai Y.Tetsu Hagané,2006; 92:83(北蓧智彦,杉本公一,向井陽一.铁と鋼,2006; 92:83) |
| [12] | Hojo T,Sugimoto K,Mukai Y.ISIJ Int,2008; 48:824 |
| [13] | Toji Y,Takagi S,Yoshino M,Hasegawa K,Tanaka Y.Mater Sci Forum,2010; 638-642:3537 |
| [14] | Qi J Y,Li Y J,Zhou H J.Trans Met Heat Treat,1984;5(1):42(齐靖远,黎永钧,周惠久.金属热处理学报,1984; 5(1):42) |
| [15] | Li G F,Dong H,Gao W,Zhao Y J.J Iron Steel Res,1996;8(5):42(李桂芬,董瀚,高伟,赵玉君.钢铁研究学报,1996; 8(5):42) |
| [16] | Li G F,Wu R G,Lei T Q.J Chin Soc Corros Prot,1991;11:27(李光福,吴忍田井,雷廷权.中国腐蚀与防护学报.1991; 11:27) |
| [17] | Chu W Y,Li S Q,Xiao J M,Wang C.Acta Metall Sin,1980; 16:179(褚武扬,李世琼,肖纪美,工枨.金属学报,1980; 16:179) |
| [18] | Nakatani Y,Higashi T,Yamada K.Fatigue Fract Eng Mater Struct,1999; 22:393 |
| [19] | Hui W J,Dong H,Weng Y Q,Wang M Q,Shi J.Trans Mater Heat Treat,2006; 27(6):37(惠卫军,董瀚,翁宇庆,王毛球,时捷.材料热处理学报,2006;27(6):37) |
| [20] | Takahashi T,Yamasaki S.Kinzoku,1997; 67:1011(高橋稔彦,山崎眞吾.金属,1997; 67:1011) |
| [21] | Suzuki N,Ishii N,Miyagawa T,Harada H.Tetsu Hagané,1993; 79:227(鈴木信一,石井伸幸,宫川敏夫,原田宏明.铁と鋼,1993; 79:227) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%