采用多道搅拌摩擦焊搭接的固态加工方法,并借助焊后表面铣削加工处理,在TC4钛合金表面制备了厚度约为500 μm的Al涂层,并对基板试样和涂层试样在700℃大气环境下进行了高温氧化实验.用扫描电镜、能谱分析和X射线衍射分析等手段研究了涂层和界面的微观组织结构,并讨论了界面中间层在高温氧化过程中的相结构演变.结果表明,经过搅拌摩擦焊搭接加工,涂层/基体的界面为富Ti的条带状结构,界面中间层厚度达60 μm.在表层富Al组织发生高温氧化及熔化现象的同时,足够厚度的Al涂层可对O的内扩散起到一定阻碍作用,而中间层的Ti和Al二元扩散行为促进了Ti-Al相在界面稀氧环境下的形成,最终起到对基体抗氧化的主要防护作用.高温氧化后表面相组成主要为Al2O3,Al2Ti和Al3Ti,而界面中间层的Ti-Al相结构呈显著的梯度分布特征.
参考文献
| [1] | Leng C Y,Zhou R,Zhang X,Lu D H,Liu H X.Acta Metall Sin,2009; 45:764(冷崇燕,周荣,张旭,卢德宏,刘洪喜.金属学报,2009; 45:764) |
| [2] | Xiong Y M,Zhu S L,Wang F H.Acta Metall Sin,2004;40:768(熊玉明,朱圣龙,王福会.金属学报,2004; 40:768) |
| [3] | Gurrappa I.Oxid Met,2003; 59:321 |
| [4] | Das D K,Trivedi S P.Mater Sci Eng,2004; A367:225 |
| [5] | Astar E,Kayali E S,Cimenoglu H.Surf Coat Technol,2008; 202:4583 |
| [6] | Li T F.High Temperature Oxidation and Hot Corrosion of Metals.Beijing:Chemical Industry Press,2004:258(李铁藩.金属高温氧化和热腐蚀.北京:化学工业出版社,2004:258) |
| [7] | Guleryuz H,Cimenoglu H.J Alloys Compd,2009; 472:241 |
| [8] | Xiao J S,Xu G D.Chin J Nonferrous Met,1997; 7:97(萧今声,许国栋.中国有色金属学报,1997;7:97) |
| [9] | Chu M S,Wu S K.Acta Mater,2003; 51:3109 |
| [10] | Xiong H P,Li X H,Mao W,Li J P,Ma W L,Cheng Y Y.Acta Metall Sin,2003:39:66(熊华平,李晓红,毛唯,李建平,马文利,程耀永.金属学报,2003; 39:66) |
| [11] | Xi Y J,Lu J B,Wang Z X,He L L,Wang F H.Trans Nonferrous Met Soc,2006; 16:511 |
| [12] | Xiong Y M,Zhu S L,Wang F H.Corros Sci,2008; 50:15 |
| [13] | Das S,Datta S,Basu D,Das G C.Ceram Int,2009; 35:1403 |
| [14] | Tian Y S,Chen C Z,Li S T,Huo Q H.Appl Surf Sci,2005; 242:177 |
| [15] | Yang M R,Wu S K.Acta Mater,2002; 50:691 |
| [16] | Charit I,Mishra R S.Mater Sci Eng,2003; A359:290 |
| [17] | Liu F C,Ma Z Y.Acta Metall Sin,2008; 44:319(刘峰超,马宗义.金属学报,2008; 44:319) |
| [18] | Jolu T L,Morgeneyer T F,Lorenzon A F G.Sci Technol Weld Join,2010; 15:694 |
| [19] | Chen Y H,Ni Q,Ke L.Trans Nonferrous Met Soc,2012;22:299 |
| [20] | Chen Y C,Nakata K.Mater Des,2009; 30:469 |
| [21] | Xiong J T,Li J L,Qian J W,Zhang F S,Huang W D.Sci Technol Weld Join,2012; 17:196 |
| [22] | Chen Y H,Ni Q.Trans China Weld Inst,2011; 32:73(陈玉华,倪泉.焊接学报,2011:32:73) |
| [23] | Schuster J C,Palm M.J Phase Equilib Diff,2006; 27:255 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%