利用OM,SEM,EDS,EBSD,硬度测试及冲击韧性实验等分析手段,对比研究H13钢和添加0.06％Nb(质量分数)H13钢(H13-Nb)芯棒偏析、液析碳化物、组织及力学性能.结果表明,与标准H13钢相比,H13-Nb中Nb加重了偏析,导致高温扩散过程偏析未能有效改善;Nb使MC液析碳化物类型由以VC为主变成以(V,Nb)C为主,提高了MC液析碳化物的析出温度,并使液析碳化物数量增加;退火态H13-Nb的严重偏析组织在淬、回火后表现为有效晶粒尺寸较大且不均匀,其较多的液析碳化物未减少;在冲击实验中,链状液析碳化物聚集的地方易产生开裂,断口上表现为横向条纹,导致韧性较低.
参考文献
| [1] | Xie Z Y.Spec Steel Technol,2010; 16(1):11(谢珍勇.特钢技术,2010; 16(1):11) |
| [2] | Akiyama M,Tsubounchi K,Tsumure M.JMater,2000; 214(2):61 |
| [3] | Wang S J.SteelPipe,1992; 27(1):45(王士俊.钢管,1992; 27(1):45) |
| [4] | Wang X J,Xu M G,Chen Q L.Shanghai Met,1998; 20(2):8(王小军,徐明纲,陈秋龙.上海金属,1998; 20(2):8) |
| [5] | Dutta B,Sellars C M.Mater Sci Technol,1987; 3:197 |
| [6] | Lu Z,Faulkner R G,Riddle N,Martino F D,Yang K.J Nucl Mater,2009; 30:445 |
| [7] | Liu J H,Ma D S,Zhang Z P,Wu L Z,Chen Z Z,Chi H X.Spec Steel,2008; 29(6):55(刘建华,马党参,张占普,吴立志,陈再枝,迟宏宵.特殊钢,2008; 29(6):55) |
| [8] | Elias C N,Da Costa Viana C S.Mater Sci Technol,1992; 8:785 |
| [9] | Hu X B,Li L,Wu X C.Heat TreatMet,2004; 29(8):13(胡心彬,李麟,吴晓春.金属热处理,2004; 29(8):13) |
| [10] | Chen Y W,Wu X C,Song W W.Trans Mater Heat Treat,2010; 31(5):75(陈英伟,吴晓春,宋雯雯.材料热处理学报,2010; 31(5):75) |
| [11] | Ma D S,Zhou J,Zhang Z K,Chi H X,Chen Z Z.Iron Steel,2010;45(8):80(马党参,周健,张忠侃,迟宏宵,陈再枝.钢铁,2010; 45(8):80) |
| [12] | Lu M H,Tian Y X,Cai H Y,Yin G H.Heat Treat Met,2010;35(8):9(陆明和,田玉新,蔡海燕,殷光虹.金属热处理,2010; 35(8):9) |
| [13] | Chi H X,Ma D S,Liu J H,Chen Z Z,Yong Q L.Acta Metall Sin,2010; 46:206(迟宏宵,马党参,刘建华,陈再枝,雍岐龙.金属学报,2010; 46:206) |
| [14] | Chen Z Z,Lan D N.Die and Mould Steel Manual.Beijing:Metallurgical Industry Press,2002:378(陈再枝,蓝德年.模具钢手册.北京:冶金工业出版社,2002:378) |
| [15] | Zhou J,Ma D S,Liu B S,Kang A J,Li X Y.Res Iron Steel,2012;(4):47(周健,马党参,刘宝石,康爱军,李向阳.钢铁研究,2012;(4):47) |
| [16] | Miao C L,Shang C J,Wang X M,Zhang L F.Acta Metall Sin,2010; 46:541(缪成亮,尚成嘉,王学敏,张龙飞.金属学报,2010; 46:541) |
| [17] | Wang C F.PhD Dissertation,Central Iron & Steel Research Institute,Beijing,2008(王春芳.钢铁研究总院博士学位论文,北京,2008) |
| [18] | Qi J J,Huang Y H,Zhang Y.Microalloyed Steel.Beijing:Metallurgical Industry Press,2006:37(齐俊杰,黄运华,张跃.微合金化钢.北京:冶金工业出版社,2006:37) |
| [19] | Li H Y,Hu J D,Li Y H.Trans Mater Heat Treat,2012; 33(1):122(李红英,胡继东,李阳华.材料热处理学报,2012; 33(1):122) |
| [20] | Yong Q L.Secondary Phases in Steels.Beijing:Metallurgical Industry Press,2006:343(雍岐龙.钢铁材料中的第二相.北京:冶金工业出版社,2006:343) |
| [21] | Hackl G.PhD Dissentation,University of Leoben,1991 |
| [22] | Shi R X,Yang R C,Yin Y S,Zhou C H.Res Iron Steel,2004; (2):34(师瑞霞,杨瑞成,尹衍升,周春华.钢铁研究,2004; (2):34) |
| [23] | Mahnken R,Schneidt A,Antretter T.Int J Plasticity,2009; 25(2):183 |
| [24] | Dong J X,Zhang M C,Zeng Y P.J Univ Sci Technol Beijing,2005; 27:197(董建新,张麦仓,曾燕屏.北京科技大学学报,2005; 27:197) |
| [25] | Liu D R,Sang B G,Kang X H,Li D 7..Acta Phys Sin,2009;58(6):104(刘东戎,桑宝光,康秀红,李殿中.物理学报,2009;58(6):104) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%