采用顶端淬火、化学相分析和热力学计算,研究了合金元素对含B特厚钢板淬透性和力学性能的影响.结果表明,由于Ti与N的结合力远高于B,微量Ti的加入(0.015％,质量分数,下同)可形成TiN,固定N元素,使B游离,提高淬透性.常规A1含量(0.02％)对N的竞争力略低于B,无法阻止BN的析出;增加Al含量至0.07％以上,可提高A1对N的结合力,固溶B含量增加,可同样起到提高淬透性的作用.通过B和固氮元素的组合,促进淬透性的提高,可使含B特厚钢板心部的显微组织状态显著改善,粒状贝氏体数量降低,马氏体/奥氏体(M/A)岛组分尺寸减小,低温冲击韧性和强度均有明显提高.
参考文献
| [1] | Li R P,Xie Y H,Shu Z.China Offshore Platform,2003; 18(3):1 (李润培,谢永和,舒志.中国海洋平台,2003;18(3):1) |
| [2] | Di G B,Liu Z Y,Hao L Q,Liu X H.MaterMech Eng,2008; 32(8):1 (狄国标,刘振宇,郝利强,刘相华.机械工程材料,2008; 32(8):1) |
| [3] | Otani K,Muroka H,Tsuruta S,Hattori K,Kawazoe H.Nippon Steel TechnolRep,1993; 58:1 |
| [4] | Sharp J V,Binlingham J,Stacey A.Marine Struct,1999; 12:349 |
| [5] | Taylor KA.ISS Trans,1993; 14:7 |
| [6] | Zhang Y Q,Zhang R J,Su H,Li L.Iron Steel,2003; 38(11):45 (张永权,张荣久,苏航,李丽.钢铁,2003;38(11):45) |
| [7] | Gao Y F.PTCA (Part A:Physical Testing),2000; 36:442 (高玉芳.理化检验-物理分册,2000; 36:442) |
| [8] | Izeki Y,Saiki K,Saiki K,Nakamura M,Ohtani H,Watanabe S.Sumitomo Search,1976; 15(5):27 |
| [9] | Iwasaki N,Tagawa H,Watanabe I,Yamada M,Nagamine T,Endo G.Nippon Kokan Technical Report Overseas,1980; 30:1 |
| [10] | Takizawa K,Kaji H,Yano K,Okano S.Shinko Steel Technical Report,1987; 3:79 |
| [11] | Chen A Z,Niu J C,Deng W P.Develop Appl Mater,2010; (1):9 (陈爱志,牛继承,邓晚平.材料开发与应用,2010; (1):9) |
| [12] | Saiga Y.ISI J Int,1989; 29:799 |
| [13] | Chen Z,Wu X C,Wang H B,Min Y A,Zhang H K.J Iron Steel Res,2008; 20(10):40 (陈卓,吴晓春,汪宏斌,闵永安,张洪奎.钢铁研究学报,2008;20(10):40) |
| [14] | Pan T,Wang X Y,Wang H,Li Y,Su H,Yang C F.J Iron Steel Res Int,2011; (suppl):242 |
| [15] | Watanabe S,Ohtani H,Kunitaki T.Trans ISIJ,1983; 23:120 |
| [16] | Paju M.Iron Steel,1992; 19:495 |
| [17] | Habu R,Miyata M,Tamukai S,Sekino S.Trans ISIJ,1983; 23:176 |
| [18] | Shen Y,Hansen S S.MetallMater Trans,1997; 28A:2027 |
| [19] | Cias W W.Metall Trans,1973; 4:603 |
| [20] | Tomita Y,Okabayashi K.Metall Trans,1986; 7A:1203 |
| [21] | Luo Z J,Shen J C,Su H,Ding Y H,Yang C F,Zhang Y Q,Ma Y.Trans Mater Heat Treat,201 0; 31 (10):63 (罗志俊,沈俊昶,苏航,丁跃华,杨才福,张永权,马跃.材料热处理学报,2010; 31(10):63) |
| [22] | Wang C F,Wang M Q,Shi J,Hui W J,Dong H.Scr Mater,2008;58:492 |
| [23] | Fang H S,Liu D Y,Bai B Z,Chang K D,Gu J L,Yang Z G.Heat Treat Met,2001; 26(10):4 (方鸿生,刘东雨,白秉哲,常开地,顾家琳,杨志刚.金属热处理,2001;26(10):4) |
| [24] | Melloy G F,Summon P R,Podgursky P E Metall Trans,1973; 4:2279 |
| [25] | Shikanai N,Kagawa H,Kurihara M.ISI J Int,1992; 32:335 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%