通过熔融玻璃净化与循环过热相结合的方法获得过冷度△T=6~280 K范围内的Fe82B17Si1共晶合金的凝固组织演变;结合突变方程和JMAK模型拟合凝固过程的冷却曲线,拟合结果符合Fe82B17Si1共晶合金的组织类型及形态随过冷度的变化规律.结果表明,当6 K≤△T<75 K时,Fes2B17Si1合金中形成了复杂规则共晶及准规则共晶组成的混合共晶组织;当75 K≤△T<180 K时,凝固组织由混合共晶组织和深过冷非规则共晶组织组成;当180 K≤△T<250 K时,凝固组织由不同含量的初生α-Fe相和枝晶间深过冷非规则共晶组织组成;当△T>250 K时,凝固组织为完全非规则共晶组织.

参考文献

[1] Yang C L,Yang G C,Lu Y P,Chen J Q,Zhou Y H.Acta Metall Sin,2005; 41:1053(杨长林,杨根仓,卢一平,陈甲琪,周尧和.金属学报,2005; 41:1053)
[2] Goetzinger R,Barth M,Herlach D M.JAppl Phys,1998; 84:1643
[3] Leonhardt M,Loser W,Lindenkreuz H G.Mater Sci Eng,1999;A271:31
[4] Lu Y P,Yang G C,Xi Z Z,Wang H P,Zhou Y H.Mater Lett,2005;59:1558
[5] Lu Y P,Yang G C,Liu F,Wang H P,Zhou Y H.Mater Lett,2007;61:987
[6] Merz G D,Kattamis T Z.Metall Trans,1977; 8A:295
[7] Croker M N,Fidler R S,Smith R W.Proc Roy Soc Lond,1973;335A:15
[8] Lu Y P,Yang G C,Liu F,Wang H P,Zhou Y H.Eur Phys Lett,2006; 74:281
[9] Lu Y P,Liu F,Yang G C,Yang C L,Zhou Y H.Appl Phys Lett,2006; 89:241902
[10] Wei B,Yang G C,Zhou Y H.Acta Metall,1991; 39:1249
[11] Chu M G,Shionara Y,Flemings M C.Metall Trans,1984; 15A:1303
[12] Murty Y,Kattamis T Z.J Cryst Growth,1974; 22:219
[13] Wang H P,Yao W J,Wei B.Appl Phys Lett,2006; 89:201905
[14] Bottinger W J,Aziz M J.Acta Metall,1989; 37:3379
[15] Battezzati L,Antonione C,Baricco M.J Alloys Compd,1997;247:164
[16] Loser W,Hermann R,Leonhardt R.Mater Sci Eng,1997; A224:53
[17] Lu Y P,Yang G C,Yang C L,Wang H P,Zhou Y H.Progress Nat Sci,2006; 16:287
[18] Duhaj P,(S)vec P.MaterSciEng,1997; A226-228:245
[19] Schroers J,Holland-Moritz D,Herlach D M.Mater Sci Eng,1997; A226-228:990
[20] Luborsky F E.Amorphous Metallic Alloys.London:Butterworth & Co.,1983:381
[21] Zhang Z Z.PhD Dissertation,Northwestern Polytechnical University,Xi'an,1993(张振忠.西北工业大学博士学位论文,西安,1993)
[22] SalehA M,Clemente RA.J Appl Phys,2004; 43:3624
[23] Emadi D,Whiting L,Djurdjevic M,Kierkus W T,Sokolowski J.MJoM,2004; 10:91
[24] Gandin Ch-A,Mosbah S,Volkmann Th,Herlach D M.Acta Mater,2008; 56:3023
[25] Yang W,Liu F,Liu H,Wang H F,Yang G C,Zhou Y H.J Cryst Growth,2009; 311:3225
[26] Liu F,Sommer F,Mittemeijer E J.JMater Sci,2004; 39:1621
[27] Xu J F,Liu F,Zhang K,Gong M M.MaterSci Technol,2012; 28:274
[28] Christian J W.The Theory of Transformation in Metals and Alloys.OXford:Pergamon Press,2002:623
[29] Xu J F,Liu F,Zhang K,Gong M M.MaterSci Technol,2012; 28:274
[30] Valiev R Z,Korasilnikov N A,Tzenev N K.Mater Sci Eng,1991;A137:35
[31] Zhang Z Z,Song G S,Yang G C.Progress Nat Sci,2000; 10:560(张振忠,宋广生,杨根仓.自然科学进展,2000; 10:560)
[32] Fras E,Lopez H F.MetallMater Trans,1999; 30B:927
[33] Saleh A M,Clemente RA.J Appl Phys,2004; 43:3624
[34] Raghavan V.Phase Diagrams of Ternary Iron Alloys Part 6A.New Delhi:Electronic Publishing Center,Green Park Extension.1993:11,406
[35] Boettinger W J,Coriell S R,Trivedi R.Principles Technol,1988;(Ⅳ):13
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%