于1mol/L LiClO4/EC+DEC电解液中添加不同的钾盐可以显著降低天然石墨电极首次循环过程中的不可逆容量损失, 提高电极的可逆容量和倍率充放电性能. 交流阻抗和电极表面固体电解质相界面(SEI)膜组分的FTIR分析表明, 添加一定量的钾盐可以降低SEI膜的锂盐含量, 有助于形成Li+迁移性良好的SEI膜.
Addition of different potassium salts into 1mol/L LiClO4/EC+DEC electrolyte can reduce the initial irreversible capacity loss at the first cycle and improve the reversible capacity and the rate capability of a natural graphite anode. Electrochemical impedance spectroscopy (EIS) and FTIR studies demonstrated the formation of a more conductive and thinner SEI layer on the graphite surface in the electrolyte containing a certain amount of potassium salt.
参考文献
| [1] | Wang Y X, Nakamura S, Tasaki K, et al. J. Am. Chem. Soc., 2002, 124: 4408--4419. [2] Nadeau G, Song X Y, Masse M, et al. J. Power Sources, 2002, 108: 86--96. [3] Lee J T, Lin Y W, Jan Y S. J. Power Sources, 2004, 132: 244--248. [4] Aurbach D, Gamolsky K, Markovsky B, et al. Electrochem. Acta, 2002, 47: 1423--1439. [5] Hu Y, Kong W, Li H, et al. Electrochem. Commun., 2004, 6: 126--131. [6] Tossici R, Berrettoni M, Rosolen M, et al. J. Electrochem. Soc., 1996, 143: L64--66. [7] Choi Y K, Chung K, Kim W S, et al. J. Power Sources, 2002, 104: 132--139. [8] Shina J S, Hana C H, Jung U, et al. J. Power Sources, 2002, 109: 47--52. [9] Aurbach D, Levi M D. J. Phys. Chem. B, 1997, 101: 4630--4640. [10] Yuasa S I, Otsuji J, Tasaka A, et al. J. Electrochem. Soc., 1998, 145: 172--176. [11] Chusid O, Ein Ely E, Aurbach D, et al. J. Power Sources, 1993, 43: 47--64. [12] Morita M, Asai Y, Yoshimoto N, et al. J. Chem. Soc., Faraday T rans., 1998, 94: 3451--3457. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%