采用IOSIPESCU纯剪切试件, 考虑纤维的编织结构和失效机理, 研究了三维机织碳/碳化硅(C/SiC)复合材料在面内剪切载荷作用下的力学性能和损伤过程. 材料具有明显的非线性应力-应变行为和残余变形等特性. 材料主要的损伤机制为基体微裂纹开裂, 界面脱粘和纤维断裂, 其中界面裂纹是材料应力-应变等力学行为的主要影响因素. 基于连续介质损伤力学分析方法, 提出了简单的损伤演化模型并对损伤演化过程进行了描述.
The mechanical behavior and damage process of a three-dimensional woven carbon/silicon carbide (C/SiC) composite under in-plane shear loading were investigated with IOSIPESCU specimens in relation with the failure mechanisms and the fiber architecture. The C/SiC composite exhibited several interesting features including an essentially non-linear stress-strain behavior and permanent deformations. The results show that the major damage mechanisms are matrix microcracks cracking, interface debonding and fiber breaking. The delamination cracks affect mainly the stress-strain behavior and the mechanical properties. A damage model is proposed based upon continuum damage mechanics to describe the damage evolution.
参考文献
| [1] | Zhang Litong, Cheng Laifei, et al. Aeronautical Manufacturing Technology, 2003, 1: 24--32. [2] Ganesh V K, Naik N K. Composite Structures, 1995, 30: 179--192. [3] Nguyen M, Herszberg I, Paton R. Compos Structures, 1999, 47: 767--779. [4] Khashaba U A. Composite Structures, 2004, 65: 167--177. [5] Sun Huiyu, Pan Ning. Composite Structures, 2005, 67: 317--322. [6] Pan Wenge, Jiao Guiqiong, et al. Journal of Inorganic Materials, 2004, 19(4): 871--875. [7] Guan Guoyang, Jiao Guiqiong, et al. Mechanical Science and Technology, 2005, 5: 515--517. [8] He Pengfei, Wu Renjie, et al. Journal of Shanghai Jiaotong University, 1994, 3: 17--22. [9] Xia Z, Curtin W A. Acta mater., 2000, 48: 4879--4892. [10] Siron O, Pailhes J, Lamon J. Composites Science and Technology, 1999, 59: 1--12. [11] Siron O, Lamom J. Acta mater., 1998, 18: 6631--6643. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%