以Fe-Ni/TiO2为催化剂,采用流化床化学气相沉积法(FBCVD)在TiO2表面原位生长碳纳米管(CNT),得到CNT/Fe-Ni/TiO2复合光催化剂.通过SEM、XRD、UV-Vis等方法表征其结构和性能,以亚甲基蓝溶液降解为模型考察其光催化性能.结果表明:Fe-Ni/TiO2催化剂在FBCVD过程中,镍主要起到了CNT生长催化活性位的作用；在生长CNT后的复合光催化剂中,比例较低的Fe3+主要作为电子俘获剂,抑制TiO2光生电子空穴的复合；Ni和CNT共同起到将电子迅速地从TiO2中导出,从而降低光生电子-空穴复合几率的作用.三者的协同作用显著改善了TiO2的光催化性能.其中Fe和Ni掺杂量分别为0.25mo1％和4.75mo1％样品的光催化活性较高,生长CNT后得到的复合光催化剂对亚甲基蓝的降解效率较纯TiO2提高约70％.
参考文献
| [1] | ZHAO Yin,LI Chun-Zhong,LIU Xiu-Hong,et al.Photosensitized degradation activity of dye by Fe-doped TiO2 nanocrystals synthesize via gas combustion flames.Journal of Inorganic Materials,2007,22(6):1070-1074. |
| [2] | YU Xiang-Yang,CHENG Ji-Jian.Photocatalytic activities of iron and chromium ion doped TiO2 films.Journal of Inorganic Materials,2001,16(4):742-764. |
| [3] | LIU Shao-You,WU Lin-Dong,ZHAO Zhong-Xing,et al.Synthesis of Ni-doped TiO2 mesoporous material via solid-state reaction at low temperature and its kinetics of methyl orange photodegradation.Journal of Inorganic Materials,2009,24(5):902-908. |
| [4] | Choi W,Termin A,Hoffmann M R.The role of metal ion dopants in quantum-sized TiO2:correlation between photoreactivity and charge carrier recombination dynamics.J.Phys.Chem.,1994,98(51):13669-13679. |
| [5] | Zhang jinlong,Wu Yongmei,Xiao Ling,et al.Properties of carbon and iron modified TiO2 photocatalyst synthesized at low temperature and photo degradation of acid orange 7 under visible light.Applied Surface Science,2010,256(13):4260-4268. |
| [6] | Garun Narungsun,Worapon Kiatkittipong,Hiroshi Yamada,et al.Hydroxylation of benzene to phenol on Fe/TiO2 catalysts loaded with different types of second metal.Catalysis Communications,2008,9(9):1886-1890. |
| [7] | Wei Fei,Wang Yao,Luo Guohua,et al.The large-scale production of carbon nanotubes in a nano-agglomerate fluidized-bed reactor.Chemical Physics Letters,2002,364(10):568-572. |
| [8] | Jung Minjae,Kwang Yong Eun,Jong Wan Park,et al.Growth of carbon nanotubes by chemical vapor deposition.Diamond and Related Materials,2001,10(3-7):1235-1240. |
| [9] | Yao Yuan,Li Gonghu,Shannon Ciston,et al.Photoreactive TiO2/carbon nanotube composites: synthesis and reactivity.Environmental Science & Technology,2008,42(13):4952-4957. |
| [10] | Gao Bin,George Z Chent,Li Gianluca.Carbon nanotubes/titanium dioxide (CNTs/TiO2) nanocomposites prepared by conventional and novel surfactant wrapping Sol-Gel methods exhibiting enhanced photocatalytic activity. Applied Catalysis B:Environmental,2009,89(3/4):503-509. |
| [11] | Wang C Y,Bottcher C,Bahnemann D W,et al.A comparative study of nanometer sized Fe(Ⅲ)-doped TiO2 photocatalysts:synthesis,characterization and activity.J.Mater.Chem.,2003,13(9):2322-2329. |
| [12] | Zhu Jiefang,Zheng Wei,He Bin,et al.Characterization of Fe-TiO2 photocatalysts synthesized by hydrothermal method and their photocatalytic reactivity for photodegradation of XRG dye diluted in water.Journal of Molecular Catalysis,2004,216(1):35-43. |
| [13] | 吴玉琪,吕功煊,李树本,等(WU Yu-Qi,et al).TiO2表面NiO光催化活性中心的构建及其光催化析氢性能研究.无机化学学报(Chinese Journal of Inorganic Chemistry),2010,26(3):476-482. |
| [14] | Yao Na,Chen Jixiang,Zhang Jianxiang,et al.Influence of support calcination temperature on properties of Ni/TiO2 for catalytic hydrogenation of ochloronitrobenzene to ochloroaniline.Catalysis Communications,2008,9(6):1510-1516. |
| [15] | Zhou Minghua,Yu Jiaguo,Chen Bei,et al.Effects of Fe-doping on the photocatalytic activity of mesoporous TiO2 powders prepared by an ultrasonic method.Journal of Hazardous Materials,2006,137(3):1838-1847. |
| [16] | Nur Azimah Jamalluddin,Ahmad Zuhalri Abdullah.Reactive dye degradation by combined Fe (Ⅲ)/TiO2 catalyst and ultrasonic irradiation:effect of Fe(Ⅲ) loading and calcination temperature.Ultrasonics Sonochemistry,2011,18(2):669-678. |
| [17] | Zhang Kan,Meng Zeda,WonchunOH.Degradation ofrhodamine B by Fe.-carbon nanotuhes/TiO2 composites under UV light in aerated solution.Chinese Journal of Catalysis,2010,31(7):751-758. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%