利用水热法在不同条件下在ITO-PET(tin-dopedindiumoxidepolyethyleneterephthalate)上制备氧化锌纳米棒阵列,通过一些定量的参数,如纳米棒的直径、长度和棒密度来表征纳米棒的形貌.通过改变反应条件可以调节上述参数.分别讨论了两个重要条件:反应时间和前驱体浓度.研究表明前驱体浓度对长径比有重要影响.柔性基底上的氧化锌纳米棒作为染料敏化电池的新型光阳极,长径比的改变对柔性电池有重要的影响.可通过调节反应条件来提高柔性染料敏化电池的性能.
ZnO nanorod arrays (ZNRs) were prepared on the tin-doped indium oxide polyethylene terephthalate (ITO-PET) by hydrothermal method under different conditions.Morphology of ZNRs was characterized by some quantitative parameters such as the diameter and length of nanorod and the density of rods.All these parameters were adjusted by changing the reaction conditions.Two important reaction conditions including reaction time and precursor concentration are discussed separately.It is demonstrated that the precursor concentration has great influence on the aspect ratio of nanorod.Flexible substrates with ZNRs are used as the novel photoanode of flexible dye-sensitized solar cells (DSCs).The aspect ratio of nanorod has major influence on the performance of flexible DSCs.The performance of flexible DSCs is improved by controlling the reaction conditions.
参考文献
| [1] | Gonzalez-Vall Irene,Lira-Cantu Monica.Vertically-aligned nanostructures of ZnO for excitonic solar cells:a review.Energy Environ.Sci.,2009,2(1):19-34. |
| [2] | Zhang Qifeng,Dandeneau Christopher S,Zhou Xiaoyuan,et al.ZnO Nanostructures for dye-sensitized solar cells.Adv.Mater.,2009,21(41):4087-4108. |
| [3] | Jiang C Y,Sun X W,Tan K W,et al.High-bendability flexible dye-sensitized solar cell with a nanoparticle-modified ZnOnanowire electrode.Appl.Phys.Lett.,2008,92(14):143101-1-3. |
| [4] | Zhang Dongshe,Yoshida Tsukasa,Oekermann Torsten,et al.Room-temperature synthesis of porous nanoparticulate TiO2 films for flexible dye-sensitized solar cells.Adv.Funct.Mater.,2006,16(9):1228-1234. |
| [5] | Law M,Greene L E,Johnson J C,et al.Nanowire dye-sensitized solar cells.Nat.Mater.,2005,4(6):455-459. |
| [6] | Jiang C Y,Sun X W,LoG Q,et al.Improved dye-sensitized solar cells with a ZnO-nanoflower photoanode.Appl.Phys.Lett.,2007,90(26):263501-1-3. |
| [7] | Hu Anzheng,Wu Fei,Liu Jinping,et al.Density-and adhesioncontrolled ZnO nanorod arrays on the ITO flexible substrates and their electrochromic performance.J.Alloys Compd.,2010,507(1):261-266. |
| [8] | Zhou Zhaoyi,Zhao Yaping,Cai Zaisheng.Low-temperature growth of ZnO nanorods on PET fabrics with two-step hydrothermal method.Appl.Surf.Sci.,2010,256(14):4724-4728. |
| [9] | Guo Min,Diao Peng,Cai Shengmin.Hydrothermal growth of perpendicularly oriented ZnO nanorod array film and its photoelectrochemical properties.Appl.Surf Sci.,2005,249(1-4):71-75. |
| [10] | Guo Min,Diao Peng,Cai Shengmin.Hydrothermal growth of well-aligned ZnO nanorod arrays:dependence of morphology and alignment ordering upon preparing conditions.J.Solid State Chem.,2005,178(6):1864-1873. |
| [11] | Greene L E,Law M,Goldberger Joshua,et al.Low-temperature wafer-scale production of ZnO nanowire arrays.Angew.Chem.Int.Ed.,2003,42(26):3031-3034. |
| [12] | Xu Chengkun,Shin Paul,Cao Liangliang,et al.Preferential growth of long ZnO nanowire array and its application in dyesensitized solar cells.J.Phys.Chem.C,2010,114(1):125-129. |
| [13] | Chao Ching-Hsun,Chan Chien-Hung,Huang Jung-Jie,et al.Manipulated the band gap of 1D ZnO nano-rods array with controlled solution concentration and its application for DSSCs.Curr.Appl.Phys.,2011,11(1):S136-S139. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%