采用失重法、电化学法和紫外-可见吸收光谱研究了3.0 mol/L H3PO4介质中,稀土Ce4+和香兰素(4-羟基-3-甲氧基-苯甲醛)对冷轧钢的缓蚀协同效应. 结果表明,香兰素对冷轧钢有中等程度的缓蚀作用,缓蚀率随其浓度的增加而增大,最大缓蚀率为66%,在钢表面的吸附符合Freundlich吸附模型;稀土Ce4+对冷轧钢的缓蚀作用较差,最大缓蚀率仅为20%左右. 稀土Ce4+和香兰素复配后对冷轧钢产生了明显的缓蚀协同效应,最大缓蚀率可达90%. 稀土Ce4+和香兰素在H3PO4介质中复配后形成了新的配合物,为混合抑制型缓蚀剂.
参考文献
| [1] | Li X H,Mu G N.Appl Surf Sci[J],2005,252:1254 |
| [2] | Walton N J,Mayer M J,Narbad A.Phytochemistry[J],2003,63:505 |
| [3] | Emregül K C,Hayval M.Mater Chem Phys[J],2004,83:209 |
| [4] | QIAN Jiu-Hong(钱九红),LI Guo-Ping(李国平).Chinese J Rare Met(稀有金属)[J],2003,27(6):813 |
| [5] | Bethencourt M,Botana F J,Calvino J J,Marcos M,Rodriguez-chacon M A.Corros Sci[J],1998,40:1803 |
| [6] | MU Guan-Nan(木冠南),LI Xiang-Hong(李向红),QU Qing(屈庆),ZHOU Jun(周俊).Acta Chim Sin(化学学报)[J],2004,62(24):2386 |
| [7] | LI Xiang-Hong(李向红),DENG Shu-Duan(邓书端),MU Guan-Nan(木冠南),FU Hui(付惠),LI Tao-Hong(李涛洪).Clean World(清洗世界)[J],2006,22(12):18 |
| [8] | Aramaki K.Corros Sci[J],2002,44:871 |
| [9] | Aramaki K.Corros Sci[J],2002,44:1361 |
| [10] | Li X H,Deng S D,Fu H,Mu G N.Corros Sci[J],2008,50:2635 |
| [11] | Mu G N,Li X M,Li F.Mater Chem Phys[J],2004,86:59 |
| [12] | WANG Bing(汪兵),LIU Qing-You(刘清友),WANG Xiang-Dong(王向东),JIA Shu-Jun(贾书君),LU Jie(卢吉),DONG Han(董翰).J Chinese Soc Corros Prot(中国腐蚀与防护学报)[J],2007,27(6):151 |
| [13] | Qu Q,Jiang S A,Bai W,Li L.Electrochim Acta[J],2007,52:6811 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%