采用共沉淀法分别制备了以对苯乙烯磺酸根、10-十一烯酸根、α-丙烯基烷基酚聚氧乙烯醚(10)硫酸根(HS-10)插层的层状双金属氢氧化物(LDH),并用X射线衍射、傅里叶红外光谱、元素分析和能谱分析测试技术表征了插层LDH的结构,用激光粒度仪和透射电子显微镜表征了在不同溶剂中LDH的分散尺寸和形貌. 结果表明,HS-10插层LDH在二甲基亚砜中分散性好,并部分剥离. 比较LDH插层剂和溶剂的Hansen溶度参数δ,表明插层剂疏水端的Hansen溶度参数与溶剂的溶度参数越接近,得到的LDH分散液越稳定;而二者Hansen溶度参数δ的极性分量(δp)和氢键分量(δh)越接近,LDH层板的剥离就越明显.
参考文献
| [1] | Carlino S.Solid State Ionics[J],1997,98:73 |
| [2] | Newman S P,Jones W.New J Chem[J],1998:105 |
| [3] | Leroux F,Besse J P.Chem Mater[J],2001,13:3507 |
| [4] | Matusinovi c' Z,Rogoi c' M,ipui c' J.Polym Degrad Stab[J],2009,94:95 |
| [5] | Chan Y N,Juang T Y,Liao Y L,Dai S A,Lin J J.Polymer[J],2008,49:4796 |
| [6] | Liu J,Chen G,Yang J.Polymer[J],2008,49:3923 |
| [7] | Ding Y,Gui Z,Zhu J,Hu Y,Wang Z.Mater Res Bull[J],2008,43:3212 |
| [8] | Manzi-Nshuti C,Wang D,Hossenlopp J M,Wilkie C A.Polym Degrad Stab[J],2009,94:705 |
| [9] | Gordijo C R,Constantino V R L,Silva D O.J Solid State Chem[J],2007,180:1967 |
| [10] | Li L,Ma R,Ebina Y,Iyi N,Sasaki T.Chem Mater[J],2005,17:4386 |
| [11] | Hibino T,Jones W.J Mater Chem[J],2001,11:1321 |
| [12] | Jobbgy M,Regazzoni A E.J Colloid Interface Sci[J],2004,275:345 |
| [13] | Acharya H,Srivastava S K,Bhowmick A K.Compos Sci Technol[J],2007,67:2807 |
| [14] | XU Yuan-Ze(许元泽)Tran(译).Van Krevelen D W(范克雷维伦)Auth(著).Properties of Polymer:Their Estimation and Correlation with Chemical Structure(聚合物的性质:性质的估算及其与化学结构的关系).Beijing(北京):Science Press(科学出版社),1981:6 |
| [15] | Brandrup J,Immergut E H,Grulke E A.Polymer Handbook[M],4th Edition,vol.3,New York:John Wiley & Sons,1999 |
| [16] | LI Xiao-Miao(李小苗),LIU Da-Zhuang(刘大壮),DONG Xue-Ru(董雪茹).Adhes China(粘接)[J],2007,28:33 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%