采用分步加料法,以甲苯二异氰酸酯(TDI)、聚乙二醇(PEG)、二羟甲基丙酸(DMPA)以及甲基丙烯酸β-羟乙酯(HEMA)为原料合成了光固化水性聚氨酯丙烯酸酯(PUA)预聚体.产物经三乙胺中和后自乳化分散于水中,体系固含量达到36%.比较了一步加料法和分步加料法对体系稳定性及涂膜性能的影响,并研究了PEG与DMPA物质的量的比对涂膜性能及固化时间的影响.结果表明,分步加料法制得的体系的稳定性要优于一步加料法;随着n(PEG)∶n(DMPA)的减小,涂膜的吸水率先减小后增大,而光泽和固化速度有所降低.另外,在同一预聚体的体系中,光引发剂的含量对涂膜固化时间的影响较大.
参考文献
| [1] | Odeberg J.;Jonsson JE.;Wesslen B.;Rassing J. .WATER-BASED RADIATION-CURABLE LATEXES[J].Journal of Applied Polymer Science,1996(2):435-445. |
| [2] | Jung SJ.;Cho WJ.;Ha CS.;Lee SJ. .Synthesis and properties of UV-curable waterborne unsaturated polyester for wood coating[J].Journal of Applied Polymer Science,1998(4):695-708. |
| [3] | Christian Decker;Frederic Masson;Reinhold Schwalm .Dual-Curing of Waterborne Urethane-Adrylate Coatings by UV and Thermal Processing[J].Macromolecular materials and engineering,2003(1):17-28. |
| [4] | Hsieh KH.;Kuo CH.;Dai CA.;Chen WC.;Peng TC.;Ho GH. .Synthesis and kinetic studies of UV-curable urethane-acrylates[J].Journal of Applied Polymer Science,2004(5):3162-3166. |
| [5] | 杨建文,曾兆华,王志明,杨小毛,陈用烈.紫外光固化水性涂料的发展概况[J].信息记录材料,2001(01):32-35. |
| [6] | 倪惠琼.UV-固化聚氨酯丙烯酸脂的结构与性能的关系研究[J].武汉大学学报(工学版),2001(05):117-120. |
| [7] | 倪惠琼,高凤彩.UV固化聚氨酯丙烯酸酯树脂的合成及其性质[J].涂料工业,2000(01):5-7. |
| [8] | R 霍尔曼;P 奥尔德林;徐茂均.印刷油墨、涂料、色漆紫外光和电子束固化配方[M].北京:原子能出版社,1996 |
| [9] | 韩仕甸,金养智,王菲.水性紫外光固化体系中光固化速度的影响因素[J].北京化工大学学报(自然科学版),2002(01):30-32. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%