采用可再生的蓖麻油先分别与三羟甲基丙烷(TMP)、甘油反应,再与TDI反应,生成端基为-NCO的蓖麻油基聚氨酯预聚体.对其-NCO含量进行测试,并采用FT-IR对材料进行定性分析.并对固化后的涂膜附着力、力学性能、耐磨性和耐水性能进行了测试.结果表明:采用甘油醇解蓖麻油合成的聚氨酯性能较好,其最佳反应时间为3～4 h,反应后-NCO含量为4.90%～5.32%,体系在-10～40℃能固化成膜,且成膜物有较好的防水性能和力学性能.
参考文献
| [1] | 甘厚磊,易长海,金雪,曹菊胜.蓖麻油基聚氨酯配合物的研究[J].粘接,2008(02):11-13. |
| [2] | D斯沃恩;秦洪万.油脂化学与工艺学[M].北京:中国轻工业出版社,1989:495-500. |
| [3] | 李志生 .蓖麻油精细化学品的开发与利用[J].江苏化工,1993,21(02):32-39. |
| [4] | Ferreira P;Pereira R;Coelho JFJ;Silva AFM;Gil MH .Modification of the biopolymer castor oil with free isocyanate groups to be applied as bioadhesive[J].International Journal of Biological Macromolecules: Structure, Function and Interactions,2007(2):144-152. |
| [5] | Qi Zhou;Lina Zhang;Ming Zhang;Bo Wang;Shaojie Wang .Miscibility, free volume behavior and properties of blends from cellulose acetate and castor oil-based polyurethane[J].Polymer: The International Journal for the Science and Technology of Polymers,2003(5):1733-1739. |
| [6] | 杨军,宋洁,李天虎.聚氨酯改性环氧树脂耐磨涂料的研制[J].电镀与涂饰,2006(06):27-30. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%