颜料不仅赋予涂膜色彩和遮盖力,还对涂料的流变性、耐候性和耐化学品性有很大影响.本研究以磷酸锌为主要防锈颜料,协同云母氧化铁灰,制备了无溶剂型环氧防腐涂料,对涂层基本性能进行了测试,并利用交流阻抗(EIS)测试技术和中性盐雾试验研究颜料体积浓度(PVC)对涂层防腐性能的影响.结果表明,当PVC小于12%时,涂层具有较好的防腐性能和耐划伤性能.
参考文献
| [1] | Blustein G;Deya MC;Romagnoli R;del Amo B .Three generations of inorganic phosphates in solvent and water-borne paints: A synergism case[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(5):1386-1397. |
| [2] | 杨宗志.磷酸锌系低/无毒防锈颜料的发展[J].中国涂料,2001(06):38-40,46. |
| [3] | 姜英涛.涂料基础[M].北京:化学工业出版社,2004:135. |
| [4] | Ting Wang;Yong-Jun Tan .Understanding electrodeposition of polyaniline coatings for corrosion prevention applications using the wire beam electrode method[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(8):2274-2290. |
| [5] | 刘志 .无溶剂超厚膜型环氧重防腐涂层的研制及耐久性能研究[D].青岛科技大学,2009. |
| [6] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004:218-220. |
| [7] | 刘安华.涂料技术导论[M].北京:化学工业出版社,2005:87. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%