以纳米氧化铟锡(ITO)为隔热功能性材料,以丙烯酸树脂为成膜剂,采用共混法将无机ITO和有机丙烯酸进行复合得到纳米ITO透明隔热涂层材料.研究了ITO不同用量对涂层可见光透过率、红外线透过率、紫外线透过率以及热学、机械性能的影响,优化了ITO在纳米透明隔热涂层中的用量,比较了不同成膜剂用量对各种性能的影响.结果表明:所制得的纳米ITO透明隔热涂膜的拉伸强度和断裂伸长率分别达到了9.28 MPa、268%.具有良好的隔热效果,可见光透过率达80%以上,红外线透过率小于10%.
参考文献
| [1] | 李宁;孟庆林;王鹏 .水性纳米隔热涂料的研制[J].热带建筑,2007,5(03):22-24. |
| [2] | 姚晨,赵石林,缪国元.纳米透明隔热涂料的特性与应用[J].涂料工业,2007(01):29-32. |
| [3] | HAE WOOK LEE;JIN HONG PARK .Composition for cutting off heat-ray,film formed thereform and method for forming the composition and the film[P].US,2006/0021548 A1,2006-02-02. |
| [4] | KUNO;HIROKO .Near infra-red shielding single or multilayer film and a coating liquid for forming the same[P].EP,0943587 A1,1999-09-22. |
| [5] | HIROMITSU TAKEDA;KENJI ADACHI;KAYO YABUKI .Coating solution for forming a film for cutting off solar radiation and the film formed therefrom[P].US,6319613,2001-04-24. |
| [6] | CHONAN;TAKESHI;ADACHI;KENJI .Sun shade and dispersion liquid for forming sun shade[P].Japan,US,20060086928,2006-04-27. |
| [7] | 胡志鹏.节能涂料:一个潜力巨大的市场[J].中国石油和化工经济分析,2006(18):64-65. |
| [8] | 赵石林;韦亚兵;许仲梓 .纳米透明隔热复合涂料及其该涂料的隔热效果测试装置[P].中国,CN1563231A,2005-01-12. |
| [9] | 陈飞霞,付金栋,韦亚兵,赵石林.纳米氧化铟锡透明隔热涂料的制备及性能表征[J].涂料工业,2004(02):48-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%