采用有机硅烷单体KH570和KH550双重改性水性环氧乳液,通过FT - IR、TGA、接触角测量仪对KH550、KH570改性所得产物及其涂膜进行表征,对改性后水性环氧乳液固化涂膜的微观结构及宏观性能进行了研究.结果表明:当KH570与KH550含量占环氧树脂的质量分数比为5∶1时,双重改性环氧乳液具有良好的贮存稳定性,其固化涂膜的耐水性、柔韧性和耐热性能得到很大改善.
参考文献
| [1] | 周继亮,张道洪,李廷成.环氧树脂的水性化技术与研究进展[J].粘接,2007(06):40-43. |
| [2] | Joseph R.Nowers;Balaji Narasimhan .The effect of interpenetrating polymer network formation on polymerization kinetics in an epoxy-acrylate system[J].Polymer: The International Journal for the Science and Technology of Polymers,2006(4):1108-1118. |
| [3] | ROBERT C;STANLEY A;RICHARD A P .Ageing of adhesive bonds with various surface treatments,Part 2:acrylic modified amine-cured resin[J].Adhesion(Barking England),2005,81:1183-1197. |
| [4] | 朱国民;王善琦 .环氧酯-丙烯酸接枝共聚物水性化的研究[J].涂料工业,1994,24(05):3. |
| [5] | 夏博文,杨军,宋洁.一种水性环氧防腐蚀涂料的研制[J].腐蚀与防护,2008(06):326-328. |
| [6] | GALLIANO F;LANDOLL D .Evaluation of corrosion protection properties of additives for waterborne expoy coatings on steel[J].Progress in Organic Coatings,2001,44:217. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%