对高原地区涂料应用现状及其老化原因进行了分析,对青藏高原地区年平均日照时数、地面气温、降水量等环境因素进行了量化分析,重点对有机涂层暴露在高原环境条件下的影响参数(太阳辐射强度、温度和湿度)进行了研究,并从光物理学和光化学原理的角度解释了涂层老化的内在机理,为提升有机涂料高原环境适应性提供了理论基础和科学依据.
参考文献
| [1] | 徐永祥,严川伟,丁杰,高延敏,曹楚南.紫外光对涂层的老化作用[J].中国腐蚀与防护学报,2004(03):168-173. |
| [2] | ARMSTRONG R D;JENKINS A T A;JOHNSON B W .An investiga tion into the UV breakdown of thermoset polyester coating using impedance spectroscopy[J].Corrosion Science,1995,37(10):1615-1625. |
| [3] | BAUER D R .Melamine/formaldehyde crosslinkers:characterization,network formation and crosslik degradation[J].Progress in Organic Coatings,1986,14:193. |
| [4] | PAPPAS S P .Weathering of coatings-formulation and evaluation[J].Progress in Organic Coatings,1989,17:107. |
| [5] | OOSTERBROEK M;LARMMERS R J;VAN DER VEN L GJ et al.Crack formation and stress development in an organic coating[J].Journal of Coatings Technology,1991,63(797):55-60. |
| [6] | Michael Osterhold;Patrick Glockner .Influence of weathering on physical properties of clearcoats[J].Progress in Organic Coatings: An International Review Journal,2001(1/3):177-182. |
| [7] | 溶剂可溶性氟聚物涂料的化学结构与耐候性(译文)[J].有机氟工业,2003 |
| [8] | 马艳秋;王仁辉;刘树华.材料自然老化手册[M].北京:中国石化出版社,2004 |
| [9] | 潘莹,张三平,周建龙,李晓刚,王玲,萧以德.大气环境中有机涂层的老化机理及影响因素[J].涂料工业,2010(04):68-72. |
| [10] | JACQUES L F E .Accelerated and outdoor/natural cxposure testing of coatings[J].Progress of Polymeric Science,2000,25(09):1337-1362. |
| [11] | DEHRI I;ERBIL M .The effect of relative humidity on the atmospheric corrosion of defective organic coating material:an EIS study with a new approach[J].J Corrosion Science,2000,42(06):969-978. |
| [12] | E. Schtitz;F. Berger;O. Dirckx .Study of degradation mechanisms of a paint coating during an artificial aging test[J].Polymer Degradation and Stability,1999(1):123-130. |
| [13] | Jon R.Schoonover;Darla Graff Thompson;Jill C.Osbron .Infrared linear dichroism study of a hydrolytically degraded poly(ester urethane)[J].Polymer Degradation and Stability,2001(1):87-96. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%