通过X射线衍射相分析和应力分析研究了WC-Co硬质合金γ相 (钴基Co-W-C固溶体) 的相转变. WC-Co硬质合金在烧结后至室温的冷却过程中γ相以扩散型机制为主进行fcc→hcp相变, 其非扩散型的Ms转变点在室温以上并接近室温, 室温下烧结态合金中hcp含量很少. 在Ms点以下, 凡引起合金中WC相与γ相间内应力变化 (加强或松驰) 的工艺因素均能导致合金γ相中hcp γ相比例的增加.
参考文献
| [1] | КудрявцеваВИ;ЦаиороваИН;ВаракинаАВ.[J].ПорошковаяМегллургия,1987(05):56. |
| [2] | Exner H E;Viswanadham;Wirmark G.Science of Hard Materials[M].New York:Plenum Press,1983:239. |
| [3] | Giameia F;Burma S;Rabin M .[J].Cobalt,1968,40(02):140. |
| [4] | Exner H E;Viswanadham;Wirmark G.Science of Hard Materials[M].New York:Plenum Press,1983:311. |
| [5] | Wumansji Y S;Fenkerstan B N;Blanjer M I et al.[J].Physical Metallurgy(Chinese Translation),1958,382 |
| [6] | Liu Shourong;Liu Yi .[J].J Mater Sci Technol,1996,12(05):398. |
| [7] | Bertil A;Henri P .[J].Metal Powder Report,1986,41(07):449. |
| [8] | 刘寿荣;刘方 .[J].金属热处理学报,1997,18(04):57. |
| [9] | Helssing Viswanadham.Proc.Int.Conf.Science of Hard Materials[M].Jackson,Wyoming,Plenum,New York,1981:931. |
| [10] | 刘寿荣,梁福起,孙景,郝建民.WC-8Co硬质合金中稀土添加剂的作用[J].中国稀土学报,1998(01):45-49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%