研究了钴渣的氨浸工艺.在钴渣氨浸过程中,用亚硫酸钠将钴渣中三价钴还原成二价钴,可较大程度地提高钴的浸出率.实验中,在氨水浓度为 14%,硫酸铵浓度为 160 g/L,液固比为 8∶1条件下,浸出液与钴渣在 70℃下反应 30 min,然后加入二倍钴量(摩尔比)的还原剂亚硫酸钠于 50℃下浸出 5 h,钴的浸出率达到了 97.46%,镍的浸出率为 95.00%.
The process for ammonia leaching of cobalt dregs was studied. In the course of ammonia leaching of cobalt dregs, the yield of cobalt can increase greatly when cobaltic(Ⅲ) is reduced to coboltous(Ⅱ) by the reductant such as sodium sulfite. In the experiment,when the concentration of ammonia water is 14%,the concentration of ammonium sulfate is 160 g/L and the ratio of liquid-solid is 8∶1, the cobalt dregs were reacted with leaching solution for 30 min at 70℃. Then double ammount of the reductant sodium sulfite with respect to the amount of cobalt (mol ratio) was added and the leaching reaction was continued for another 5 h at 50℃. The yield of cobalt and nickel are 97.46% and 95.00%, respectively.
参考文献
| [1] | 栾广英;关晓宇.[J].有色金属(冶炼部分),1993(03):15. |
| [2] | 王鹏伟.钴渣选择性酸溶抑制铜铁的研究与实践[J].矿冶,1998(01):38. |
| [3] | 李洪桂.[J].稀有金属与硬质合金,1991(03):32. |
| [4] | 杨新生.氨浸过程浅析[J].有色矿冶,1993(01):34-38. |
| [5] | 《浸矿技术》编辑委员会.浸矿技术[M].北京:原子能出版社,1994:147. |
| [6] | 中南矿冶学院分析化学教研室.化学分析手册[M].北京:科学出版社,1982:576. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%