采用电化学方法和慢应变速率拉伸(SSRT)技术, 研究了时效制度对1420 Al-Li合金的时效动力学及抗应力腐蚀性能的影响.通过透射电镜、扫描电镜观察与分析, 探讨了不同时效处理工艺下1420合金的显微组织、慢应变速率拉伸断口形貌及其影响机制.结果表明, 与120 ℃/12 h相比, 采用120 ℃/6 h+190 ℃/6 h处理不仅可以缩短合金到达时效峰值的时间, 提高合金的强度, 使其断裂强度、断裂时间、延伸率以及总断裂能等都得到显著提高, 同时也改善了合金的抗应力腐蚀性能.
参考文献
| [1] | DEJONG H F.A survey of the development and applications of aluminium-lithium alloys[J].Aluminium,1984(09):673. |
| [2] | Wang Z F;Zhu Z Y;Ke W.Stress corrosion cracking of an Al-Li alloy[J].Metallurgical and Materials Transactions,1992(23):3337. |
| [3] | Sheppard T;Parson N C.Corrosion resistance of Al-Li Alloys[J].Materials Science and Technology,1987(03):341. |
| [4] | Harris S J.The Status of Al-Li Alloy[A].U.S.A,1984:219. |
| [5] | Batrakov V P.Strength profile in Al-Li plate material[J].Protection of Metals,1981(07):128. |
| [6] | ФРИДЛЯНДеРИΗ.Al-Mg-Li alloy 1420[J].Light Alloy,1990(02):60. |
| [7] | 许鹤鸣;何德茂.金属热处理[M].北京:机械工业出版社,1989:38. |
| [8] | Cui Yusheng .New light alloy of Al-Mg-Li[J].Scripta Materialia,1996,34(05):781. |
| [9] | 顾景诚;洪永先.Al-Mg-Li 系1420合金[J].轻合金,1990(02):60. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%