研究了含稀土Tb的多晶Ni50Mn29Ga21磁性形状记忆合金的磁感生应变效应.在一定的应力状态下,可获得-1.1%的大磁感生应变.稀土在明显地细化晶粒和提高材料力学性能的同时,不影响马氏体孪晶界面的运动,反而使应力作用下的磁感生应变效应进一步提高,使材料更具有实用性.
参考文献
[1] | Ullakko K;Huang J K;Kantner C et al.Large magnetic-fieldinduced strains in Ni2MnGa single crystals[J].Applied Physics Letters,1996,69:1966. |
[2] | Tickle R.;James R.D. .Ferromagnetic shape memory in the NiMnGa system[J].IEEE Transactions on Magnetics,1999(5):4301-4310. |
[3] | Wu GH;Yu C H;Meng L Q et al.Giant magnetic-field-induced strains in Heusler alloy NiMnGa with modified composition[J].Applied Physics Letters,1999,75:2990. |
[4] | Yu CH.;Chen JL.;Wu GH.;Yang FM.;Tang N.;Qi SR.;Zhan WS. Wang Z.;Zheng YF.;Zhao LC.;Wang WH. .Magnetic-field-induced strains and magnetic properties of Heusler alloy Ni52Mn23Ga25[J].Journal of Applied Physics,2000(9 Pt.3):6292-6294. |
[5] | Murray S J;Marioni M;Allen S M et al.6% magnetic-fieldinduced strain by twin-boundary motion in ferromagnetic Ni-MnGa[J].Applied Physics Letters,2000,77:886. |
[6] | LIANG Ting,XU Hui-Bin,JIANG Cheng-Bao,GONG Sheng-kai.Preparation and Properties of the Ni2MnGa Magnetic Shape Memory Alloy[J].中国物理快报(英文版),2000(04):296-297. |
[7] | ULLAKKOK;HuangJK;KokorinVV et al.Magnetically controlled shape memory effect in Ni2MnGa intermetallics[J].Scripta Materialia,1997,36:1133. |
[8] | Ezera Y;Sozinov A;Kimmel G .Magnetic shape memory (MSM) effect in textured polycrystalline Ni2MnGa[A].Newport Beach,California,1999,3675:244. |
[9] | Ullakko K;Ezer Y;Sozinov A et al.Magnetic-field-induced strains in polycrystalline Ni-Mn-Ga at room temperature[J].Scripta Materialia,2001,44:475. |
[10] | O'Handley RC.;Marioni M.;Nembach H.;Allen SM.;Murray SJ. .Phenomenology of giant magnetic-field-induced strain in ferromagnetic shape-memory materials (invited)[J].Journal of Applied Physics,2000(9 Pt.2):4712-4717. |
[11] | Likhacher A A;Ullakko K .Quantitative model of large magnetostrain effect in ferromagnetic shape memory alloys[J].the European Physical Journal B,2000,14:263. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%