采用外补偿法改善Nd-Fe-B永磁材料的磁性能温度稳定性.讨论了磁温度补偿合金与永磁体组合后的磁性能和温度稳定性的表征.研究表明: 用组合磁体的最大磁能积可以表征其磁性能, 用开路法测试的可逆磁通温度系数可表征组合磁体的磁性能温度稳定性.用本实验室开发的磁温度补偿合金得到的组合磁体的可逆磁通温度系数小于0.001%/℃(20～100 ℃), 室温下的最大磁能级达到195 kJ·m-3.外补偿法不仅能够有效地改善Nd-Fe-B永磁材料的磁性能温度稳定性, 而且能够保持较高的磁性能.
参考文献
| [1] | Kim AS.;Lizzi T.;Camp FE. .HYDROGEN INDUCED CORROSION MECHANISM IN NDFEB MAGNETS[J].Journal of Applied Physics,1996(8 Pt.2a):4840-4842. |
| [2] | Kim A.S.;Camp F.E. .The role of oxygen for improving magnetic properties and thermal stability of sintered (Nd,Dy)(Fe,Co)B magnets[J].IEEE Transactions on Magnetics,1995(6):3656-3658. |
| [3] | Mottram R S;Williams A J;Harris I R .Blending additions of cobalt to Nd16Fe76B8 milled powder to produce sintered magnets[J].Journal of Magnetism and Magnetic Materials,2000,217(01):27. |
| [4] | 成问好,李卫,李传健,郭朝晖,赵文彤.制取低温度系数Nd-Fe-B磁体的混合合金法工艺[J].稀有金属材料与工程,2002(01):52-55. |
| [5] | Li Y;Evans H E;Irris L R et al.The oxidation of NdFeB magnets[J].Oxidation of Metals,2003,59(1-2):167. |
| [6] | 李平,敖晖,曲选辉.钕铁硼用磁温度补偿合金的成分[J].中国有色金属学报,2004(z3):41-44. |
| [7] | 敖晖,李平,曲选辉.计算机模拟辅助设计陀螺仪用磁温度补偿合金[J].中国有色金属学报,2004(z3):56-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%