采用真空自耗重熔法制备了V5Cr5Ti合金,测试了V5Cr5Ti合金的高温拉伸性能,分析了高温拉伸断口的宏观、微观形貌,探讨了钒合金的断裂机理.结果表明:随温度升高,V5Cr5Ti合金的强度性能下降,塑性性能先降低后升高;在700～900 ℃,V5Cr5Ti合金仍具有良好的强韧性综合性能;其高温断口特征表现为韧性断裂为主,韧性和脆性特征共存的现象.
参考文献
| [1] | 邱励俭.纵观国际核聚变进展探讨中国核聚变发展的道路[J].力学进展,1999(04):471. |
| [2] | Loomis B A;Smith D L;Garner F A .Swelling of neutron-irradiated vanadium alloys[J].Journal of the Nuclear Material,1991,179-181:771. |
| [3] | Satou M;Abe K;Kayano H .High-temperature deformation of modified V-Ti-Cr-Si type alloys[J].Journal of the Nuclear Material,1991,179-181:757. |
| [4] | Hoelzer D T;West M K;Zinkle S J;Rowcliffe A F .Solute interactions in pure vanadium and V4Cr4Ti alloy[J].Journal of the Nuclear Material,2000,283-287:616. |
| [5] | Hoelzer D T;Rowcliffe A F .Investigation solute interactions in V-4Cr-4Ti based on tensile deformation behavior of vanadium[J].Journal of the Nuclear Material,2002,307-311:596. |
| [6] | 何肇基.金属的力学性质[M].北京:冶金工业出版社,1989 |
| [7] | 刘瑞堂;刘文博;刘津云.工程材料力学性能[M].哈尔滨:哈尔滨工业大学出版社,2001 |
| [8] | 冶金工业部钢铁研究院.难熔金属断口分析图谱[M].北京:科学出版社,1978 |
| [9] | 孙智;江利;应鹏展.失效分析-基础与应用[M].北京:机械工业出版社,2005 |
| [10] | 崔约贤;王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%