通过恒温氧化实验研究了氢化锆在350～600℃纯氧中的氧化行为,分析了温度和时间对氧化层质量增重的影响规律,并借助Ⅺm,SEM等分析测试手段对氧化层的物相组成和截面形貌进行分析.结果表明,氢化锆的质量增重随着氧化温度的升高而增大,450℃以下,氧化反应速度很慢;500'～600℃温度范围内,氢化锆的质量增重与氧化时间的关系曲线符合抛物线规律.氧化层由内到外分为致密层和疏松层,氧化层主要由单斜相M-zeO2组成.
参考文献
| [1] | 陈鹤鸣;马春来 .纯锆在400～850℃纯氧中的氧化[J].核科学与工程,1982,2(01):72. |
| [2] | Moya J S;Diaz M;Bartolome J F;Roman E Sacedon J L Izquierdo J.Zirconium oxide film formation on zircaloy by water corrosion[J].Acta Materialia,2000(48):4749. |
| [3] | Kenji Konashi;Tamio Ikeshoji .A molecular dynamics study of thermal conductivity of zirconium hydride[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(0):279-282. |
| [4] | Yamanaka S;Yoshioka K;Uno M;Katsura M Anada H Matsuda T Kobayashi S.Thermal and mechanical properties of zirconium hydride[J].Journal of Alloys and Compounds,1999(293-295):23. |
| [5] | Li Y S;Wong P C;Mitchell K A R .XPS investigations Of the interaefiom of hydrogen with thin fihm of zirconium oxide[J].Applied Surface Science,1995,89:263. |
| [6] | Eigenk M S;Paramonov D V.An analysis Of disassembling the radial reflector of a thermionic space nuclear reactor power system[J].Nuclear Safety,1994(35):74. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%