通过对钛合金进行大的塑性变形获得了TB2丝材, 分别对TB2丝材进行直接时效和固溶时效处理. 发现经过大的塑性变形后获得了具有良好综合性能的TB2丝材, 尤其是对丝材进行直接时效处理后, 其抗拉强度最高可达1690 Mpa, 同时具有良好的延性性能. 金相观察结果显示, 经过大变形直接时效后的晶粒为等轴状, 比固溶时效后的组织更为细密. 采用大变形和直接时效的方法来获得高强度高韧性良好配合的材料应具有稳定的面心立方或体心立方结构, 低的应变硬化指数, 较高的回复温度和有效的硬化机制.
参考文献
| [1] | Fischer FD.;Werner E.;Tanaka K.;Cailletaud G.;Antretter T.;Reisner G. .A new view on transformation induced plasticity (TRIP)[J].International Journal of Plasticity,2000(7-8):723-748. |
| [2] | Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409. |
| [3] | Zhou Y G;Zeng W D;Yu H Q.A new high-temperature deformation strengthening and toughening process for titanium alloys[J].Materials Science and Engineering,1996:58. |
| [4] | Hall O .The deformation and ageing of mild steel (Ⅲ):Discussion of results[J].Proc Phys Soc London B,1951,64:747. |
| [5] | Petch N .The cleavage strength of poly crystals[J].Journal of the Iron and Steel Institute,1953,174:25. |