采用多层多道搭接的激光熔覆方法在0Cr18Ni10Ti不锈钢表面上分别熔覆两种镍基合金涂层.1#合金涂层的硬度在HRC34左右,无开裂;2#合金涂层的硬度在HRC47左右,易开裂.采用硬度较低的1#合金涂层作为过渡层成功解决了2#合金涂层的开裂问题,成功制备出大面积较厚涂层.经光学显微镜(OM)、X射线衍射(XRD)、扫描电子显微镜(SEM)以及能谱(EDS)分析可知,大面积熔覆层的表层主要由γ-Ni枝晶、块状γ-Ni和M12C型碳化物增强相组成.显微硬度测试表明,表层平均硬度达HV0.2583,自熔覆层表层至基体,显微硬度逐渐降低.
参考文献
| [1] | 石世宏,傅戈雁.不锈钢表面激光熔覆层耐腐蚀研究[J].金属热处理,1999(03):14-16. |
| [2] | Ski Shihong;Zheng Qiguang;Fu Geyan;Wang Xinlin .Comparison study on resistance to wear and abrasion of high-temperature sliding strike of laser and plasma spray layer on the stainless steel surface[J].Nuclear Engineering and Design,2004,231:121. |
| [3] | 王新林,李必文,郑启光.核阀密封面激光熔覆层耐磨性能研究[J].应用激光,2003(05):261-264. |
| [4] | 刘蓉,陶锡麒,潘邻,夏春怀,曹庆,谷文.激光熔覆与等离子喷焊WF218合金的组织和性能比较[J].材料保护,2004(05):48-49. |
| [5] | Jussi Vikstrom .Galling resistance of hardfacing alloys replacing Stellite[J].Wear,1994,179:143. |
| [6] | Persson D H E;Jacobson S;Hogmark S.Effect of temperature on friction and galling of laser processed Norem 02 and Stellite 21[A].,2003:498. |
| [7] | 曾大文,夏辉,谢长生.Ni基合金激光熔覆层组织特征及凝固过程的研究[J].稀有金属材料与工程,2000(02):109-113. |
| [8] | 赵海云,王华明.激光熔覆过渡金属硅化物Laves相增强高温耐磨抗氧化涂层组织与性能研究[J].应用激光,2002(02):89-92. |
| [9] | Yang Y. .Microstructure and properties of laser-clad high-temperature wear-resistant alloys[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,1999(1/2):19-23. |
| [10] | 张庆茂 .送粉激光熔覆应用基础理论的研究[D].中国科学院长春光学精密机械与物理研究所,2000. |
| [11] | 查莹,周昌炽,唐西南,张展.改善激光熔覆镍基合金和陶瓷硬质相复合涂层性能的研究[J].中国激光,1999(10):947-950. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%