对Mo-Si-Al-K合金板坯经过20%, 40%, 50%轧制及退火后掺杂粒子的演变过程、 不同掺杂量(与金属钼的质量百分比AKS-1:K(%) =0.08，AKS-3:K(%) =0.27，AKS-5:K(%)=0.45)板坯的力学性能进行研究,结果表明:轧制板坯中的掺杂相沿轧制方向拉长、碎化,形成沿轧制方向排列的掺杂粒子列;适当地增加掺杂量能显著提高板坯的抗拉强度、延伸率及杯突值;随着掺杂量的增加,加工成型的难度加大.
参考文献
| [1] | 彭志辉.钨、钼材料物理冶金基础[A].长沙:中南大学出版社,2003:10. |
| [2] | 向铁根.钼的物理性质,钼冶金[M].长沙:中南大学出版社,2002:5. |
| [3] | Iorio L E;Bewlay B P;Larsen M .Doped particle characterization and bubble evolution in aluminum-potassium-silicon-doped molybdenum wire[J].Metallurgical and Transations A,2002,33A:3349. |
| [4] | 张久兴,周美玲,周文元,王金淑,聂祚仁,左铁镛.稀土钼合金力学和热发射性能的研究[J].稀有金属,2002(02):124-128. |
| [5] | Ju Choi;Jae-Hoon Lee;In-Huang Moon;Hyung Sup Chol .The process of bubble formation in the hot isostatic pressing treated,doped molybdenum wire[J].Metallurgical and Transations A,1990,21A:919. |
| [6] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1982:119. |
| [7] | MYOUNG KI YOO;YUTAKA HIRAOKA;JU CHOI .Recrystallization of Molybdenum Wire Doped with Potassium-Silicate[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1995(4):801-816. |
| [8] | 宋晓艳,谷南驹,刘国权,王宝奇.第二相粒子含量对基体晶粒长大影响的计算机仿真研究[J].金属学报,2000(06):592-596. |
| [9] | 朱亮,张爱华.钢中脆硬粒子裂纹形成机理[J].物理学报,2004(02):571-576. |
| [10] | 李静,高家诚,王勇.掺杂提高钼丝再结晶温度的研究进展[J].稀有金属与硬质合金,2003(01):22-24,42. |
| [11] | Bewlay B P;Lewis N;Lou K A .Observation on the evolution of potassium bubble in tungsten ingots during sintering[J].Metallurgical and Transations A,1992,23A:121. |
| [12] | 毛小南,周廉,曾泉浦,魏海荣.TiCp颗粒增强钛基复合材料的强化机理研究[J].稀有金属材料与工程,2000(06):378-381. |
| [13] | 陈强,李大成,卜春阳.掺杂Si-Al-K对钼粉及其烧结制品组织、性能的影响[J].稀有金属,2007(03):300-305. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%