采用新的包套热轧工艺方法,在普通轧机上成功制备出厚度为1.9 mm的高铌钛铝合金薄板,总变形量达到80%以上.整个轧制过程保持在近等温的状态下,平均轧制速率小于80 mm·s-1.显微组织观察表明,薄板组织均匀,轧制变形后的晶粒度略大于合金变形前的晶粒度.在动态再结晶与道次间回炉处理时发生的静态再结晶两种机制的作用下,发生了完全再结晶,因而不再具备变形组织的带状特征.板材的取向图显示存在<100>晶向平行于轧制方向的晶粒,其余晶粒的取向则呈现随机分布.锻态高铌钛铝合金包套热轧后织构组分存在{100}<010>的立方织构,这种织构是由再结晶引起的.
参考文献
[1] | Kim Y W;Dimiduk D M .Progress in the understanding of gamma titanium aluminides[J].JOM-Journal of the Minerals Metals and Materials Society,1991,43(08):40. |
[2] | Kim Y W .Ordered intermetallic alloy,Part Ⅱ:Gamma titanium aluminides[J].JOM-Journal of the Minerals Metals and Materials Society,1994,12(07):7. |
[3] | Liu Z C;Lin J P;Li S J;Cheng G L .Effect of Nb and Al on the microstructures and mechanical properties of high Nb containing TiAl based alloys[J].Intermetallics,2002,10:653. |
[4] | Apple F;Paul D H;Oehring Michael;Chemens H .Physical metallurgy of high Nb-containing TiAl alloys[J].Zeitschrift fur Metallkunde,2004,95(07):585. |
[5] | Koeppe C.;Clemens H.;Schretter P.;Glatz W.;Bartels A. .OPTIMIZING THE PROPERTIES OF TIAL SHEET MATERIAL FOR APPLICATION IN HEAT PROTECTION SHIELDS OR PROPULSION SYSTEMS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(1/2):182-193. |
[6] | Clemens H;Kestler H;Eberhardt N.Processing of γ-TiAl based alloys on an industrial scale[A].,1999 |
[7] | Semiatin S L;Ohis M;Kerr W R .Temperature transients during hot pack rolling of high temperature alloys[J].Scripts Metall Mater,1991,25:1851. |
[8] | Gopal D;Kesfler H;Clemens H .Bartolotta P A Sheet gamma TiAl:status and opportunities[J].JOM-Journal of the Minerals Metals and Materials Society,2004,11(56):42. |
[9] | 缪家士,林均品,王艳丽,林志,陈国良.高铌钛铝基合金板材的高温包套轧制[J].稀有金属材料与工程,2004(04):436-438. |
[10] | Bartels A;Schillinger W .Micromechanical mechanism of texture formation in γ-TiAl[J].Intermetallics,2001,9:883. |
[11] | Appol F;Wagner R .Microstructure and deformation of twophase γ-titanium Aluminidas[J].Materials Science and Egnineering,1998,R22:187. |
[12] | Bartels A;Uhlenhut H .Anisotropy of plastic flow in strongly textured γ-TiAl based alloys[J].Intermetallica,1998,6:685. |
[13] | Cerling R;Barrels A;Clemens H .Structural characterization and tensile properties of a high niobium containing gamma TiAl sheet obtained by powder metallurgical processing[J].Intermetallics,2004,12:275. |
[14] | Schillinger W;Bartels A;Cerling R;Schimansky F P Clemens H .Texture evolution of the γ-and the α/α2-phase during hot rolling of γ-TiAl based alloys[J].Intermetallics,2006,14:336. |
[15] | Bartels A;Hartig C H;Willems S T .Influence of the deformation conditions on the texture evolution in gamma-TiAl[J].Materials Science and Engineering,1997,A239-240:14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%