以直接电解脱氧法(FFC法)电解氧化镝制取金属镝工艺为主要研究范畴.实验以烧结Dy2O3试样为阴极,高纯石墨棒为阳极,于CaCl2熔盐中电解脱氧.结合电脱氧理论系统研究了试样的成型压力、烧结温度以及烧结时间对所得阴极电解过程及产物脱氧率的影响.同时,结合对各条件下阴极片体的微观形貌的分析结果及电脱氧产物XRD谱图分析,得到了阴极制备工艺的适宜条件.实验结果表明:直接电脱氧法制备金属镝工艺是可行的,微孔阴极中的颗粒连通性好、颗粒尺寸小、孔隙率高均有利于电脱氧进行.实验得到的最佳电极制备条件为:成型压力为15 MPa、烧结温度为1200℃、烧结时间为8 h.
参考文献
| [1] | 张世荣.金属镝的制备、提纯及应用[J].稀有金属与硬质合金,2000(03):53-59. |
| [2] | 林河成.金属镝材料的生产及应用[J].有色冶炼,2002(02):32-35. |
| [3] | 候庆烈;王振华 .稀土金属的制备与提纯研究进展[J].上海有色金属,1999,20(03):132. |
| [4] | 黄礼煌.稀土提取技术[M].北京:冶金工业出版社,2006:372. |
| [5] | 金红.低成本金属钛生产方法的研究与开发[J].稀有金属,2000(04):296-300. |
| [6] | Chen G Z;Fray D J;Farthing T W .Direct electrochemical reduction of titanium dioxide to titanium in molten calcium chloride[J].NATURE,2000,407:361. |
| [7] | Fray D J;Farthing T W;Chen G Z .Removal of oxygen from metal oxides and solid solution by electrolysis in a fused salt[P].PCT/GB99/01781,1998. |
| [8] | 彭金辉,范兴祥,郭胜惠,张利波,张世敏.二氧化钛直接电解提取钛短流程绿色新技术[J].稀有金属,2002(04):290-293. |
| [9] | 刘美凤,郭占成,卢维昌.TiO2直接电解还原过程的研究[J].中国有色金属学报,2004(10):1752-1758. |
| [10] | 杜继红,奚正平,李晴宇,李争显,唐勇.掺杂的TiO2阴极对熔盐电解的影响[J].稀有金属,2007(03):336-340. |
| [11] | Fenn A J;Cooley G;Fray D .Exploiting the FFC Cambridge process[J].Advanced Materials & Processes Article,2004,162:2. |
| [12] | Liu Meifeng;Guo Zhancheng;Lu Weichang .An investigation into electrochemical reduction of TiO2 pellet[J].Trans Inst Min Metall C,2005,114:87. |
| [13] | Wang Shulan;Li Yingjun .Reaction mechanism of direct electroreduction of titanium dioxide in molten calcium chloride[J].Journal of Electroanalytical Chemistry,2004,547:37. |
| [14] | Fray D J;Chen G Z .Reduction of titanium and other metal oxides using electrodeoxidation[J].MST,2004,20:295. |
| [15] | LIU Meifeng,LU Shigang,KAN Surong,LI Guoxun.Effect of electrolysis voltage on electrochemical reduction of titanium oxide to titanium in molten calcium chloride[J].稀有金属（英文版）,2007(06):547-551. |
| [16] | Schwandt C;Fray D J .Determination of the kinetic pathway in the electrochemical reduction of titanium dioxide in molten calcium chloride[J].Electrochimica Acta,2005,51:66. |
| [17] | Chen G Z;Fray D J .A morphological study of the FFC chromium and titanium powders[J].Trans Inst Min Metall Sect C:Miner Process Extr-Metall,2006,115:49. |
| [18] | 刘军;佘国政.粉末冶金与陶瓷成型技术[M].北京:化学工业出版社,2005:3. |
| [19] | 刘美凤,卢世刚,阚素荣.熔盐电解直接制备钛铬合金的研究[J].稀有金属,2008(04):526-530. |
| [20] | 曹战民,朱鸿民,乔芝郁.相图及其在钛电解新工艺和钛合金设计中的应用[J].稀有金属快报,2007(09):1-5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%