采用机械合金化方法制备MmNi3.9Co0.45Mn0.4Al0.25-CoB复合储氢合金.通过X射线衍射(XRD)分析、扫描电子显微镜(SEM)分析、充放电及线性极化测试.研究了球磨时间对复合储氢合金相结构及电化学性能的影响.研究结果表明:随着球磨时间的增加,复合储氢合金的衍射峰逐渐宽化,杂散衍射峰消失,表现出非晶化趋势;复合储氢合金颗粒尺寸变小,并星球状均匀分布.电化学测试结果表明:当球磨时间达到45 min时,复合储氢合金具有较好的活化及高倍率放电性能,30次循环容量保持卒最高,达到90.66%,表现出良好的电化学动力学性能及催化活性.但当球磨时间过长时,合金颗粒出现相互粘连及团聚的情况,局部出现较大结块,导致复合合金电极的交换电流密度降低.
参考文献
| [1] | Jurczyk M;Smardz L;Smardz K;Nowak M Jankowska E .Nanocrystalline LaNi5-type electrode materials for Ni/MH,batteries[J].Journal of Solid State Chemistry,2003,171(1-2):30. |
| [2] | Ma X B;Wei X D;Dong H;Liu Y N .The relationship between discharge capacity of LaNi5 type hydrogen storage alloys and formation enthalpy[J].Journal of Alloys and Compounds,2010,490(1-2):548. |
| [3] | B.Joseph;B. Schiavo .Effects of ball-milling on the hydrogen sorption properties of LaNi_5[J].Journal of Alloys and Compounds,2009(2):912-916. |
| [4] | 许剑轶,阎汝煦,罗永春,张胤,陈江平.A2B7型La0.75Mg0.25Ni3.5-xFex（x=0～0.3）贮氢合金相结构及电化学性能研究[J].稀有金属,2009(03):323-327. |
| [5] | 孔祥成,吴铸,杜俊霖,夏广林,倪君.铁取代部分铬对TiVCrMn合金储氢性能的影响[J].稀有金属,2009(05):644-647. |
| [6] | Wu G.;Li N.;Dai CS.;Zhou DR. .Electrochemical preparation and characteristics of Ni-Co-LaNi5 composite coatings as electrode materials for hydrogen evolution[J].Materials Chemistry and Physics,2004(2/3):307-314. |
| [7] | Deng C;Shi PF;Zhang S .Effect of surface modification on the electrochemical performances of LaNi5 hydrogen storage alloy in Ni/MH batteries[J].Materials Chemistry and Physics,2006(2/3):514-518. |
| [8] | Feng H W;Liu X D;Tian X;Chi B,Huang L H,Xu J .Electrechemical properties of the Mm0.3Ml0.7Ni3.55Co0.75Mn0.4 Al0.3 alloy mixed with Ni powder[J].International Journal of Hydrogen Energy,2009,34(04):1886. |
| [9] | 韩树民,赵敏寿,吴耀明,郑炀曾.利用球磨制备AB2-AB5复合贮氢合金及其电极性能和微观结构研究[J].无机化学学报,2003(03):262-266. |
| [10] | Li H;Liu J;Xie SH;Qiao MH;Dai WL;Li HX .Highly active Co-B amorphous alloy catalyst with uniform nanoparticles prepared in oil-in-water microemulsion[J].Journal of Catalysis,2008(1):104-110. |
| [11] | Y. D. Wang;X. P. Ai;Y. L. Cao;H. X. Yang .Exceptional electrochemical activities of amorphous Fe–B and Co–B alloy powders used as high capacity anode materials[J].Electrochemistry communications,2004(8):780-784. |
| [12] | Yi Liu;Yijing Wang;Lingling Xiao;Dawei Song;Yaping Wang;Lifang Jiao;Huatang Yuan .Structure and electrochemical behaviors of a series of Co-B alloys[J].Electrochimica Acta,2008(5):2265-2271. |
| [13] | Feng Y;Jiao L F;Yuan H T;Zhan M .Study on the preparation and dectrechemical characteristics of MgNi-CoB alloys[J].Journal of Alloys and Compounds,2007,440(1-2):304. |
| [14] | Yongfeng Liu;Hongge Pan;Mingxia Gao;He Miao;Yongquan Lei;Qidong Wang .Function of Al on the cycling behavior of the La-Mg-Ni-Co-type alloy electrodes[J].International journal of hydrogen energy,2008(1):124-133. |
| [15] | Mu D;Yang C;Shen B L;Jiang H .Oxidation resistance of botided pure cobalt[J].Journal of Alloys and Compounds,2009,479(1-2):629. |
| [16] | Zheng G.;White RE.;Popov BN. .APPLICATION OF POROUS ELECTRODE THEORY ON METAL HYDRIDE ELECTRODES IN ALKALINE SOLUTION[J].Journal of the Electrochemical Society,1996(2):435-441. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%