采用金相显微镜(OM)、扫描电镜(SEM)对Mg-Y合金与纯镁的铸态凝固组织进行了观察,并采用X射线衍射仪(XRD),能谱分析仪(EDS)对合金在凝固过程中形成的相进行了分析,利用析氢法及电化学方法研究了Mg-Y合金与纯镁在3.5％的NaCl溶液中的腐蚀行为.结果表明,纯镁的晶粒比较粗大,合金的晶粒比纯镁小,合金由灰白色的初生α相和深色的共晶组织构成,以及少量呈颗粒状弥散分布在基体中Mg24Y5相.析氢法中,试样在浸泡了8h左右时,合金腐蚀速率是纯镁的2.85倍,纯镁在浸泡7h后pH值稳到10.4左右,而合金的pH值变化较快,在1.5h后就已经达到了10.4,最后稳定在11.2左右.从腐蚀形貌看,纯镁的腐蚀较浅,沿表面扩展,呈纹理状,合金则呈现明显的局部腐蚀特征,表面形成了严重的腐蚀坑.3.5％的NaCl溶液中测得的极化曲线可以得出,合金的腐蚀电流Icorr (4.05 ×10 - A·cm-2)比纯镁Icirr(6.81×10-5 A·cm-2)要高的多.
参考文献
| [1] | 郭全英,刘正,毛萍莉,孙晶.挤压态Mg-13Gd-4Y-0.4Zr合金高温时效析出机制[J].稀有金属,2010(02):197-201. |
| [2] | 刘正;张奎;曾小勤.镁基轻质合金理论基础及应用[M].北京:机械工业出版社,2002:10. |
| [3] | Zhao M C;Liu M;Song G L .Influence of pH and chloride ion concentration on the corrosion of Mg alloy ZF41[J].Corrosion Science,2008,50:3168. |
| [4] | Chang J W;Guo X W;He S M;Fu P H .Investigation of the corrosion for Mg-xGd-3Y-0.4Zr (x=6,8,10,12 wt％) alloys in a peak-aged condition[J].Corrosion Science,2008,50:166. |
| [5] | Lin P Y;Zhou H;Li W P;Li W Zhao S Z Su J G .Effect of yttrium addition on the oxide scale of AM50 magnesium alloy[J].Corrosion Science,2009,51:1128. |
| [6] | Zhao M C;Schmutz P;Brunner S;Liu M Song G L Atrens A .An exploratory study of the corrosion of Mg alloys during interrupted salt spray testing[J].Corrosion Science,2009,51:1277. |
| [7] | Cheng Y L;Qin T W;Wang H M;Zhang Z .Comparison of corrsion behaviors of AZ31,AZ91,AM 60 and ZK60 magnesium alloys[J].Transactions of Nonferrous Metals Society of China,2009,19:517. |
| [8] | 于生海 .AZ系镁合金在模拟海水介质中的腐蚀行为[D].重庆大学,2008. |
| [9] | Li Z Q;Shan D Y;Chen R S;Ke W,Han E H .Corrosion behavior of WE54 magnesium alloy in 3.5％NaCl solution[J].Transactions of Nonferrous Metals Society of China,2006,16:s1806. |
| [10] | 张景怀,唐定骧,张洪杰,王立民,王军,孟健.稀土元素在镁合金中的作用及其应用[J].稀有金属,2008(05):659-667. |
| [11] | 丁文江,向亚贞,常建卫,彭颖红.Mg-Al系和Mg-RE系合金在NaCl溶液中的腐蚀电化学行为[J].中国有色金属学报,2009(10):1713-1719. |
| [12] | 樊昱,吴国华,高洪涛,李冠群,翟春泉.La对AZ91D镁合金力学性能和腐蚀性能的影响[J].金属学报,2006(01):35-40. |
| [13] | Song Y W;Shan D Y;Chen R S;Han E H .Corrosion characterization of Mg-8Li alloy in NaCl solution[J].Corrosion Science,2009,51:1087. |
| [14] | 宋光铃.镁合金的腐蚀与防护[M].北京:化学工业出版社,2006:112. |
| [15] | 褚凤清,王国平.牙科金属与合金腐蚀研究方法的进展[J].国际口腔医学杂志,2010(02):189-191,195. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%