优化设计了4种不同Re含量的耐腐蚀定向镍基高温合金,含Re分别为0％,1％,2％和3％(质量分数).对比了不同Re含量合金的铸态枝晶、γ’相形貌及持久性能试样的断口筏排化组织,测试了不同Re含量合金热处理态的980℃/200 MPa持久寿命,研究了Re对耐腐蚀镍基定向合金组织及持久寿命的影响.研究表明:随着Re含量的增加,合金的一次枝晶间距减小；γ’相尺寸减小,立方化程度增加；蠕变试样的筏排组织更加细化、完善与稳定,因此,合金持久寿命提高.
参考文献
| [1] | Cetel A D;Duhl D N.Second generation columnar grain nickel-base superalloy[A].,1992:287. |
| [2] | Ross E W;O'Hara K S.Rene'142:a high strength,oxidation resistance DS turbine airfoil alloy[A].,1992:257. |
| [3] | Harris K;Erickson G L.Development of the rhenium containing superalloys CMSX-4 & CM186 LC for single crystal blade and directional solidified vane application in advanced turbine engines[A].,1992:297. |
| [4] | Kobayashi T;Sato M;Harada H.Development of a third generation DS superalloy[A].,2000:323. |
| [5] | Toshiharu Kobayashi;Yutaka Koizumi;Tadaharu Yokokawa .Development of a 4th Generation DS Superalloy[J].日本金属学会誌,2002(9):897-900. |
| [6] | Bügel R;Grossmann J;Lüsebrink O.Development of a new alloy for directional solidification of large industrial gas turbine blades[J].The Superalloys,2004(25) |
| [7] | 骆宇时 .Re在单晶高温合金中的强化机理[D].北京:北京航空材料研究院,2006. |
| [8] | 骆宇时,李嘉荣,刘世忠,孙凤礼,韩梅,曹春晓.铼对单晶高温合金γ、γ'相的影响[J].钢铁研究学报,2007(06):61-64. |
| [9] | 骆宇时,李嘉荣,刘世忠,曹春晓.Re对单晶高温合金蠕变过程中γ'相定向粗化的影响[J].材料工程,2006(07):43-46,50. |
| [10] | 骆宇时,李嘉荣,刘世忠,孙凤礼,曹春晓.Re对单晶高温合金持久性能的强化作用[J].材料工程,2005(08):10-14. |
| [11] | 李金山,张万明,寇宏超,李双明,张丰收,胡锐,刘林,傅恒志.原始组织对高温合金热处理组织和力学性能的影响[J].中国有色金属学报,2002(02):290-293. |
| [12] | 蒋立武,李树索,邱自成,韩雅芳.拉晶速率对Ni3Al基单晶合金IC6SX凝固组织和高温持久性能的影响[J].金属学报,2009(05):547-552. |
| [13] | 顾家琳,郭彦宏,贾崇林,施惠基.组织结构对Ni-20Cr-10Mo-10Co高温合金高温力学性能的影响[J].稀有金属材料与工程,2003(02):103-107. |
| [14] | 王建涛,骆合力,李尚平,曹栩,张喜娥.冷却速率对MX246A合金组织和持久性能的影响[J].铸造,2010(04):355-357. |
| [15] | Nabarro Frank R N .Rafting in superalloys[J].Metallurgical and Materials Transactions,1996,27A:513. |
| [16] | Giamei A F;Anton D L .Rhenium additions to a Ni-base superalloy:effct on microsturecture[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16A:1997. |
| [17] | Pollock T M;Argon A S .Creep behavior of Ni-base singlecrystal superlloys[J].Acta Metallurgica Et Materialia,1994,42:1859. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%