采用真空分段烧结法制备了两种不同粒度的高单相Cr2AlC化合物粉末,并使用超音速火焰喷涂(HVOF)方法在GH4169高温镍合金上制备了Cr2 AlC涂层,对喷涂粉末及涂层进行了相结构分析,测试了涂层的显微硬度、孔隙率,并采用扫描电子显微镜(SEM)对喷涂粉末及涂层截面形貌进行了观察,结合扫描电镜能谱仪(EDS)和X射线衍射研究了涂层相组成,分析了粉末粒度对涂层微观组织结构的影响.研究结果表明:采用超音速火焰喷涂成功制备了厚度超过200μm的Cr2 AlC涂层,涂层与基体紧密结合,涂层微观组织致密,采用较细的粉末有利于得到更高致密度的涂层.在喷涂过程中,有少量Cr2AlC粉末发生分解形成Cr7C3化合物.
参考文献
| [1] | Barsoum M W .The MN+1AXN phases:a new class of solids,thermodynamically stable nanolaminates[J].Progress in Solid State Chemistry,2000,28(1-4):201. |
| [2] | Wang J;Zhou Y .Recent progress in theoretical prediction,preparation,and characterization of ltyered ternary transition-metal carbides[J].Annual Review of Materials Research,2009,39:415. |
| [3] | Z.J. Lin;M.S. Li;J.Y. Wang .High-temperature oxidation and hot corrosion of Cr_2AlC[J].Acta materialia,2007(18):6182-6191. |
| [4] | Cui B;Jayaseelan D D;Lee W E .Microstructural evolution during high-temperature oxidation of Ti2A1C ceramics[J].Acta Materialia,2011,59(10):4116. |
| [5] | Frodelius J;Sonestedt M;Bjorklund S;Palmquist JP;Stiller K;Hogberg H;Hultman L .Ti2AlC coatings deposited by High Velocity Oxy-Fuel spraying[J].Surface & Coatings Technology,2008(24):5976-5981. |
| [6] | Sonestedt, M;Frodelius, J;Palmquist, JP;Hogberg, H;Hultman, L;Stiller, K .Microstructure of high velocity oxy-fuel sprayed Ti2AlC coatings[J].Journal of Materials Science,2010(10):2760-2769. |
| [7] | Frodelius J;Johansson E M;Córdoba J M;Odén M Eklund P Hultman L .Annealing of thermally sprayed Ti2 AlC costinga[J].International Journal of Applied Caramic Technology,2011,8(01):74. |
| [8] | Li, J.J.;Hu, L.F.;Li, F.Z.;Li, M.S.;Zhou, Y.C. .Variation of microstructure and composition of the Cr_2AlC coating prepared by sputtering at 370 and 500°C[J].Surface & Coatings Technology,2010(23):3838-3845. |
| [9] | Wang, QM;Renteria, AF;Schroeter, O;Mykhaylonka, R;Leyens, C;Garkas, W;to Baben, M .Fabrication and oxidation behavior of Cr2AlC coating on Ti6242 alloy[J].Surface & Coatings Technology,2010(15):2343-2352. |
| [10] | Q.M. Wang;R. Mykhaylonka;A. Flores Renteria;J.L. Zhang;C. Leyens;K.H. Kim .Improving the high-temperature oxidation resistance of a β-γ TiAl alloy by a Cr_2AlC coating[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(11):3793-3802. |
| [11] | 饶琼,周香林,张济山,孙东柏.超音速喷涂技术及其应用[J].热加工工艺,2004(10):49-52. |
| [12] | 陈建强,刘敏,邓春明,邓畅光.喷距对低温高速火焰喷涂Ti涂层的影响[J].稀有金属,2011(06):835-840. |
| [13] | Wang X H;Zhou Y C .High-temperature oxidation behavior of Ti2AIC in air[J].Oxidation of Metals,2003,59(03):303. |
| [14] | Lee D B;Nguyen T D .Cyclic oxidation of Cr2AlC between 1000 and 1300 ℃ in air[J].Journal of Alloys and Compounds,2008,464(1-2):434. |
| [15] | D.B. Lee;Thuan Dinh Nguyen;J.H. Han;S.W. Park .Oxidation of Cr_2AlC at 1300 ℃ in air[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(10):3926-3934. |
| [16] | Lee D B;Park S W .Oxidation of Cr2 AlC between 900 and 1200 ℃ in air[J].Oxidation of Meals,2007,68(05):211. |
| [17] | Lin Z J;Li M S;Wang J Y;Zhou Y C .High-temperature oxidation and hot ocrrosion of Cr2AlC[J].Acta Materialia,2007,55(18):6182. |
| [18] | Wang, QM;Renteria, AF;Schroeter, O;Mykhaylonka, R;Leyens, C;Garkas, W;to Baben, M .Fabrication and oxidation behavior of Cr2AlC coating on Ti6242 alloy[J].Surface & Coatings Technology,2010(15):2343-2352. |
| [19] | 张富文,秦国义,王文静.超音速气雾化AgNi10粉末的微观分析[J].稀有金属,2005(02):211-213. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%