钛铁矿型焊条成本低,焊接时电弧稳定,焊缝成形美观、熔渣覆盖度好,熔敷效率较高,对焊缝中的锈、油污等不敏感,但抗裂性能差,影响焊接质量.针对钛铁矿型焊条熔敷金属抗裂性差的问题,将12种不同含量的稀土镧(La)及氧化铈(CeO2)过渡到钛铁矿型焊条药皮中,在螺旋式压涂机上将其压涂成钛铁矿型电焊条.按照国家标准制取试板并截取冲击及拉伸样坯,对12种熔敷金属进行了冲击试验和拉伸试验.采用扫描电镜(SEM)对含La/CeO2稀土的拉伸断口形貌进行观察,用能谱仪(EDS)分析断口夹杂物化学成分组成.结合熔敷金属的宏观力学性能,分析熔敷金属断裂的相关信息.结果表明:不含稀土的熔敷金属拉伸断口韧窝较浅,尺寸小些,熔敷金属抗拉强度、延伸率和-20℃下的冲击功分别是467.9 MPa,27％和27 J.其他加入稀土的断口可见韧窝变大变深,夹杂物尺寸变小.但La和CeO2加入的量要适当,不是越多越好,当La,CeO2在药皮中的含量分别是0.5％和0.1％时,和不加入稀土的配方相比,熔敷金属的抗拉强度提高了6.36％,延伸率提高了25.1％,冲击功提高了54.4％,成本仅提高了6.3％,具有较大的推广价值.
参考文献
| [1] | 田文彤.半固态触变模锻7A04合金的力学性能[J].锻压技术,2012(05):63-66. |
| [2] | 黄正华,戚文军,郑开宏,张新明,刘敏,余志明.La对ZK60合金铸态组织与力学性能的影响[J].稀有金属,2012(05):835-840. |
| [3] | 李秀程,谢振家,王学林,王学敏,尚成嘉.高强度低碳贝氏体钢拉伸断口分离现象及机理研究[J].金属学报,2013(02):167-174. |
| [4] | C. San Marchi;B.P. Somerday;X. Tang;G.H. Schiroky .Effects of alloy composition and strain hardening on tensile fracture of hydrogen-precharged type 316 stainless steels[J].International journal of hydrogen energy,2008(2):889-904. |
| [5] | CM. Younes;A.M. Steele;J.A. Nicholson;C.J. Barnett .Influence of hydrogen content on the tensile properties and fracture of austenitic stainless steel welds[J].International journal of hydrogen energy,2013(11):4864-4876. |
| [6] | 郭凡,郭鸿镇,姚泽坤,田宏杰,赵张龙.热处理对Ti2AlNb/Ti60双合金接头组织及性能的影响[J].锻压技术,2013(03):137-140. |
| [7] | 韩丰霞,雷霆,周林,黄世弘,吕改改.30MVA直流电弧炉冶炼钛渣配碳比研究[J].稀有金属,2012(02):297-303. |
| [8] | LIU Yingying,YAOZekun,GUO Hongzhen.Effect of near isothermal forging on the microstructure of Ti3Al/TC11 welding interface[J].稀有金属（英文版）,2009(05):471-477. |
| [9] | YE Dameng,XIONG Weihao,Zhang Xiuhai,QU Jun,YAO Zhenghua.Microstructure and shear strength of the brazed joint of Ti(C,N)-based cermet to steel[J].稀有金属（英文版）,2010(01):72-77. |
| [10] | WU Huiqiang,Feng Jicai,He Jingshan,ZHOU Li.Microstructural characterization of electron beam welded joints of TiAl-based intermetallic compound[J].稀有金属（英文版）,2005(01):82-86. |
| [11] | YANG Shanglei,XUE Xiaohuai,LOU Songnian,CHEN Yan,LI Shimin.Electron beam welding of Re and BT5-1 titanium alloy[J].稀有金属（英文版）,2005(03):293-297. |
| [12] | Guo-Li Liang,Shan-Wu Yang,Hui-Bin Wu,Xue-Li Liu.Microstructure and mechanical performances of CGHAZ for oil tank steel during high heat input welding[J].稀有金属（英文版）,2013(02):129-133. |
| [13] | 吕滨,于学成,吴琼,姜志刚,臧颖波,王凯.添加剂在四氯化钛气相氧化过程中的作用机制[J].稀有金属,2012(05):780-784. |
| [14] | 郭永环,范希营,高顶.氧化铈对低合金钢焊条熔敷金属的影响[J].机械工程学报,2009(04):285-289. |
| [15] | 范希营,郭永环.氧化铈对低合金钢焊条焊缝硫磷的影响[J].焊接学报,2010(12):70-72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%