采用多步交换反应方法,将聚丙烯酸丁酯(PBA)嵌入到白泥(高岭土和白云母的混合物)的高岭土层间,白泥的结构变化用X射线衍射进行了表征. 将所得白泥-PBA层状混杂物与热塑性弹性体丁苯三嵌段共聚物(SBS)在160 ℃共混,制得了新型混杂纳米复合热塑性弹性体. 在白泥-PBA的质量分数为0.5%～6.0%范围内,复合弹性体的拉伸强度、断裂伸长率及高温玻璃化转变温度Tg2分别由15.70 MPa、598.3%和96 ℃升高至26.76 MPa、846.0%和156 ℃,而低温玻璃化转变温度Tg1仍保持为-76 ℃,透明度也保持不变.
参考文献
| [1] | Shi H,Pinnavia T J. Chem Mater,1996,8:1584 |
| [2] | Vaia R A,Jandt K D,Kramer E J, et al. Chem Mater,1996,8:2628 |
| [3] | Usuki A,Kato M,Okada A, et al. J Appl Polym Sci,1997,63:137 |
| [4] | Messermith P B,Giannelis E P. J Polym Sci,Part A:Polym Chem,1995,[ STHZ]33:1047 |
| [5] | 陈中华(CHEN Zhong-Hua),黄承亚(HUANH Cheng-Ya),龚克成(GONG Ke-Cheng) . 合成橡胶工业(Hecheng Xiangjiao Gongye),1998,21 (2):116 |
| [6] | 陈中华(CHEN Zhong-Hua). [博士学位论文](Doctoral Dissertation). 广州 (Guangzhou):华南理工大学(South China University of Technology),1998 |
| [7] | Tunney J J,Detellier C. J Mater Chem,1996,6(10):1679 |
| [8] | Vaia R A,Teukolsky R K,Giannelis E P. Chem Mater,1994,6:1017 |
| [9] | Honeker C C,Thomas E L. Chem Mater,1996,8:1702 |
| [10] | Krishnamoorti R,Vaia R A,Giannelis E P. Chem Mater,1996,8:1728 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%