采用研磨固相反应法制备LaCoyMn1-yO3钙钛矿型复合氧化物纳米微粒.利用XRD、TG-DTA、TEM技术研究了LaCoyMn1-yO3的形成过程，并考察了微粒形貌及其平均粒径.用交流阻抗法和磁天平测定了样品的电导率和磁化率，结果表明，当取代量y=0.5时，其电导与磁化率均最小，并初步作了机理探讨.
The nanophase LaCoyMn1-yO3 0≤y≤1) has been prepared by solid state reaction and characterized by XRD, TG/DTA, TEM and atomic absorption spectrometry. The results showed that the compound is of perovskite type and the crystals of some samples are distored, but not collapsed.The AC impedance and magnetic balance results indicated that when y = 0. 5 the compound has minimum value both in conductivity and magnetic susceptibility, which was interpreted in terms of minimum value of unpaired electron number of the compound at this condition.
参考文献
| [1] | ZenerC. PhysRev,1951,182(3):403 |
| [2] | Takahashi T,Iwahara H,Suzuui T Proc 3rd Intern Symp Fuel Cell ,Brussels .Belgium, 1969:113 |
| [3] | Ohno Y, Nageta S, Sato H. Solid State Ionics,1981,3/4:4 |
| [4] | yon Helmhoet R,Weckers J,Halzapfel B. et al.Phys Rev Lett, 1993,71:1331 |
| [5] | Takeda Y,Hoshino Y,Kawahara T, et al. J Mater Sci Lett,1992,11(16):1113 |
| [6] | Lin P-Y,Peng J,Hou B-H, et al. J Phys Chem,1993,97(8): 12471 |
| [7] | Manoharan S S,Vasanthacharya N Y,Hegde M S,et al. J Appl Phys,1994,76(6):3923 |
| [8] | Xiong G C,Zhang B, Wu S C, et al. J Mater Chem,1995,5(7) :1089 |
| [9] | LEI Li-Xu (雷立旭),XIN Xin-Quan (忻新泉).Huaxue Tongbao (化学通报),1997,(2)：1 |
| [10] | LI Qing-Wen (李清文),LI Juan (李娟),XIA Xi (夏熙).Huaxue Xuebao (化学学报),1999,57(5)：491 |
| [11] | Jonker G H. J Appl Phys,1996,37(3):1424 |
| [12] | Bard A J,Faulkner L R,Auths (著).Gu Lin-Ying (谷林瑛),et al 译(Trans). Electrochemical Methods-Fundamental and Applications (电化学方法原理与应用).Beijing (北京)：Chemical Industrial Press (化学工业出版社),1986 |
| [13] | LIU She-Tian (刘社田),YUZuo-Iong (于作龙),YU Ya-Ii (于亚利).Huaxue Xuebao (化学学报),1993,51:543 |
| [14] | ZHANG Ruo-Hua (张若华)Auth (著).SHEN Pan-Wen (申泮文)Proof (校).Rare-earth Element Chemistry (稀土元素化学).Tianjin (天津)：Tianjin Science-Technology Press (天津科学技术出版社),1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%