用固相合成法制备了层状前驱体钠锰氧化物(Na0.67[Mn0.90Mg0.10]O2),研究了它在LiCl*H2O-LiNO3熔融盐体系和LiBr*2H2O正己醇溶液体系中与Li+的交换反应动力学特点. 采用XRD技术检测前驱体及交换产物的浓度变化. 用插层反应动力学模型算出不同反应温度的熔融盐体系和正己醇体系中离子交换反应的表观速率常数,分别为0.127～0.208 s-1(260～300 ℃)和5.93×10-4～3.94×10-3 s-1(40～80 ℃);反应级数为1.24～1.30和0.92～1.13;反应活化能为31.2 和43.7 kJ/mol. 讨论了2个体系动力学行为的异同点,初步确定Li+→Na+过程是离子交换反应速率的控制步骤.
参考文献
| [1] | Armstrong A R,Bruce P G. Nature[J],1996,381:499 |
| [2] | Hwang S J,Park H S,Choy J H. Chem Mater[J],2000,12:1 818 |
| [3] | Chitrakar R,Kanoh H,Kim Y S, et al. J Solid State Chem[J],2001,160:69 |
| [4] | Guenne L B,Deniard P,Biensan P, et al. J Mater Chem[J],2000,10:2 201 |
| [5] | Hwang S J,Park H S,Choy J H. J Phys Chem B[J],2000,104:7 612 |
| [6] | Delmas C,Braconnier J J,Maazaz A, et al. Rev Chim Mine[J],1982,19:343 |
| [7] | Hooley J G. Carbon[J],1973,11:225 |
| [8] | Riekel C,Reznik H G,Schollhorn R. J Solid State Chem[J],1980,34:253 |
| [9] | O′Hare D,Evans J S O,Price S. J Chin Chem Soc[J],1998,45:591 |
| [10] | Robertson A D,Armstong A R,Bruce P G. J Am Chem Soc,Chem Commun[J],2000:1 997 |
| [11] | Hulbert S E. J Br Ceram Soc[J],1969,6:11 |
| [12] | Stephen J P,John S O E,Robin J F, et al. Adv Mater[J],1996,8:582 |
| [13] | Andrew M F,Victoria M G,Howard G H, et al. Adv Mater[J],1999,11:1 466 |
| [14] | Clark S M,Irvin P,Flaherty J, et al. Rev Sci Instrum[J],1994,65:2 210 |
| [15] | Clark S M,Evans J S O,O′Hare D, et al. J Am Chem Soc,Chem Commun[J],1994:809 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%