采用溶液缩聚法由酰氯端基聚醚酮酮(PEKK)齐聚物和4,4′-二苯氧基二苯砜(DPODPS)制备了PEKK/DPODPS多嵌段共聚物,用DSC、TGA等方法对共聚物进行了表征和性能测试.结果表明,随着共聚物中DPODPS含量的增加,共聚物的熔融温度逐渐降低,而其玻璃化转变温度则逐渐升高.当DPODPS质量分数在32.63%～40.73%范围内时,所得共聚物的Tg为185～193℃,比纯PEKK的Tg高出20～28℃;其Tm为322～346℃,比纯PEKK的Tm降低35～59℃,这既保持了纯PEKK的耐热性,又改善了熔融加工性能.该组成范围内的共聚物的拉伸强度(σt)为86.6～84.2 MPa,拉伸模量(M)为3.1～3.4 GPa,断裂伸长率(ε)为18.5%～20.3%.
参考文献
| [1] | Stenning T C. Mod Plast[J] ,1986,11:86 |
| [2] | Jansons V,Gors H C. WO 84/03 891 [P], 1984 |
| [3] | Moore S,Jansons V,Dahl K. WO 86/01 199[P] ,1986 |
| [4] | Jurgen K, Rober L, Gerhand H. EP 0 327 980 [P], 1989 |
| [5] | SHENG Shou-Ri(盛寿日),CAI Ming-Zhong(蔡明中),SONG Cai-Sheng(宋才生).Acta Polym Sin(高分子学报)[J],1998,(5):616 |
| [6] | LI Wei(黎苇),CAI Ming-Zhong(蔡明中),SONG Cai-Sheng(宋才生).Chin J Appl Chem(应用化学)[J],2002,19:653 |
| [7] | Claek J H,Denness J E. Polymer[J],1994,35:2 432 |
| [8] | Mikhail G Z, Javier D A, Julio C A, et al. J Polym Sci, Polym Chem Edn[J],1998,36:1 251 |
| [9] | Sun K P,Sang Y K. Macromolecules[J] ,1998,31:385 |
| [10] | Hale W F, Farnham A G, Johnson R N. J Polym Sci A-1 [J],1967,5:2 399 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%