通过溶胶-凝胶法合成了纳米级CoTiO3,并将其用于K2FeO4电极的改性. 电化学测试结果表明,掺杂质量分数为20%的CoTiO3不但能够提高K2FeO4电极的放电电位平台(150 mV左右),还能保持一定放电容量. 虽然Co(Ⅱ)可以被高铁酸钾氧化成Co(Ⅲ),造成实际参与放电的活性物质的量减少,但Co(Ⅲ)可有效维持K2FeO4高电位放电的性能.
参考文献
| [1] | Licht S,Wang B H,Ghosh S. Science[J],1999,285:1 039 |
| [2] | Licht S,Wang B H,Gosh S, et al. Electrochem Commun[J],1999,1:522 |
| [3] | Licht S,Naschitz V,Ghosh S. J Phys Chem B[J],2002,106:5 947 |
| [4] | Licht S,Wang B H,Ghosh S, et al. Electrochem Commun[J],2000,2:535 |
| [5] | Licht S,Tel-Vered R,Halperin L. Electrochem Commun[J],2002,4:933 |
| [6] | Licht S,Ghosh S,Naschitz V. Electrochem Solid-State Lett[J],2001,4:A209 |
| [7] | Licht S,Wang B H,Xu G, et al. Electrochem Commun[J],1999,1:527 |
| [8] | Delaude L,Laszlo P. J Org Chem[J],1996,61:6 360 |
| [9] | Licht S,Maschhitz V,Lin B, et al. J Power Sources[J],2001,99:7 |
| [10] | LIU Xian-Ming(刘献明),YAO Hai-Jun(姚海军),ZHANG Xiao-Gang(张校刚), et al. Chin J Inorg Chem(无机化学学报)[J],2003,19:257 |
| [11] | Behl W K,Toni J E. J Electroanal Chem[J],1971,31:63 |
| [12] | Yang W H,Wang J M,Zhang Z B, et al. Chin Chem Lett[J],2002,13:761 |
| [13] | Licht S,Ghosh S. J Power Sources[J],2002,109:465 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%