用正丁醇改性合成了高相容性TDI-三聚体,克服了单纯TDI-三聚体与羟基丙烯酸树脂混溶性差的缺点,用所合成产物与羟基丙烯酸树脂配漆,漆膜微粒细小均匀. 当采用自制催化剂、温度控制在60 ℃、n(-NCO)∶n(-OH)在10∶ 1左右时,得到固体含量在50%左右,二甲苯容忍度大于2.3、游离TDI含量小于1.5%的TDI-三聚体. 产物的热重分析结果表明,随-NCO与-OH摩尔比的增加,产物热稳定性增加;催化剂种类对产物热稳定性的影响不大,但产物的热稳定性随催化剂用量的增加而增加.
参考文献
| [1] | Sheehan D,Bentz A. J Appl Polym Sci[J],1962,6(19):47 |
| [2] | Semsarzadeh M A,Navarchian A H. J Appl Polym Sci[J],2003,90:963 |
| [3] | Mothè C G,Araùjo C R de. Thermochim Acta[J],2000,357～358:321 |
| [4] | Font R,Fullana A,Caballero J A, et al. J Anal Appl Pyroly[J],2001,58～59:63 |
| [5] | Sonal D,Thakore I M,Sarawade B D, et al. Eur Polym J[J],2000,36:711 |
| [6] | Bilbao R,Mastral J F,Ceamanos J, et al. J Anal Appl Pyroly[J],1996,37:69 |
| [7] | JIN Chao(金超),LI Wei-Shan(李伟善),YANG Xin-Hong(杨新宏). Polyurethane Ind(聚氨酯工业)[J],2004,19(4):9 |
| [8] | Ewald M,Windmueller M,Poersch W, et al. US 0 135 007A1[P],2003 |
| [9] | JIN Ping(金平),QIU Fang-Zheng(邱方正),CHEN Jian-Ding(陈建定). J Func Polym(功能高分子学报)[J],2000,13:285 |
| [10] | LI Shao-Xiong(李绍雄),ZHU Lü-Min(朱吕民)Auth(著). Polyurethane Resin(聚氨酯树脂)[M]. Nanjing(南京):Jiangsu Press For Science and Technology(江苏科学技术出版社),1992:405 |
| [11] | CHEN Jing-Hua(陈精华),LIU Wei-Qu(刘伟区),XUAN Yi-Ning(宣宜宁), et al. Chin J Appl Chem(应用化学)[J],2004,21(6):629 |
| [12] | SONG Chun-Mei(宋春梅),WANG De-Ning(王得宁),PAN Tie-Ying(潘铁英). Acta Polym Sin(高分子学报)[J],2002,3:319 |
| [13] | HE Xin-Zhao(何新照),WANG Zhi-Jun(王志军). Chin Paint Coat Ind(涂料工业)[J],1996,4:19 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%