制备了晶态层状(甘氨酸-N,N-双亚甲基膦酸-磷酸氢)锆(α-ZGDMPP),层间距为1.52 nm,研究了α-ZGDMPP对正丁胺的插层性能.用元素分析、X射线衍射、红外光谱、固体核磁共振谱13C CP/MAS NMR和热分析测试技术对α-ZGDMPP和插层复合物进行了表征.结果表明,α-ZGDMPP具有不同于α-ZP的形成主-客化合物的插层性能,正丁胺的插入使α-ZGDMPP的层间距增大1.02 nm,插入的正丁胺呈双分子层排列,碳链与层板夹角约为55°,在150～250℃从层板中脱出.
参考文献
| [1] | Clearfield A,Smith G D. Inorg Chem[J] ,1969,8:431 |
| [2] | Poojary D M,Shpeizer B,Clearfield A. J Chem Soc Dalton Trans[J] ,1995:111 |
| [3] | Clearfield A,Robert M T,Debra K, et al. J Chem Faraday Trans[J] ,1985,81:545 |
| [4] | Ferragina C, Cafareui P, Destefanis A, et al. J Therm Anal Calor[J] ,2003,71:1 023 |
| [5] | Duan X,Li F,He J, et al. J Poro Mater[J],2002,9:5 |
| [6] | Kumar C V,Chaudhari A. JAm Chem Mater[J] ,2001,13(2) :2 383 |
| [7] | Xu Q H,Fu L S,Li L S, et al. JMater Chem[J] ,2000,10:2 532 |
| [8] | LUO Bi-Kui(罗必奎) ,FU Xiang-Kai(傅相锴). Ion Exch Adsorp(离子交换与吸附)[J],1995,11(2) :162 |
| [9] | Ma X B,Fu X K. J Mol Cata A:Chem[J],2004,208:129 |
| [10] | Sui Y,Fu X K,Zeng R Q, et al. J Mol Cata A:Chem[J],2004,217:133 |
| [11] | Moedrzer K,Irani R R J. Org Chem[J] ,1966,31:1603 |
| [12] | NING Yong-Cheng(宁永成). Stuctural Identification of Organic Compounds and Organic Spectroscopy( 有机化合物结构鉴定与有机波谱学)[M].Beijing(北京):Sience Press(科学出版社),1998 |
| [13] | Alberti G.Acc Ghem Res[J],1978,11:163 |
| [14] | HU Hong-Wen(胡宏纹).Organic Chemistry(有机化学),Vol.1(上册)[M].Beijing(北京):Higher Education Press(高等教育出版社),1990 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%