以聚环氧乙烷/高氯酸锂络合物(PEO/LiClO4)为基体,前驱体正硅酸乙酯(TEOS)在基体中水解缩合的同时加入偶联剂KH560改性原位生成的SiO2,制备了PEO/LiClO4/KH560-SiO2聚电解质膜,采用SEM、AFM、DSC和交流阻抗方法研究了改性前后聚电解质膜的表面形貌、结晶度和电导率. 结果表明,改性SiO2在PEO中分散均匀且粒径仅为35 nm,不同SiO2含量下改性后的聚电解质膜电导率均比改性前明显提高. 当SiO2质量分数为10%时,PEO/LiClO4/KH560-SiO2的电导率达到最大值4.8×10-5 S/cm(30 ℃).
参考文献
| [1] | Scrosati B,Croce F,Persi L.J Electrochim Society [J],2000,147:1 718 |
| [2] | Sung H Y,Wang Y Y,Cheng Z L.J Electrochim Society [J],1998,145:1 718 |
| [3] | Ji K S,Moon H S,Kim J W,et al.J Power Source [J],2003,117:124 |
| [4] | Forsyth M,MacFarlane D R,Best A,et al.Solid State Ionics [J],2002,147:203 |
| [5] | Eliana Q,Piercarlo M,Aldo M.Solid State Ionics [J],1998,110:1 |
| [6] | SHEN Xin-Zhang(沈新璋),JIN Ming-Hui(金名惠).Chinese J Appl Chem(应用化学) [J],2003,20(10):1003 |
| [7] | Liu Y,Lee J Y,Hong L.J Power Sources [J],2004,129:303 |
| [8] | XU Xian-Hua(徐先华),PAN Chun-Yue(潘春跃),FENG Qin(冯庆),et al.Chinese J Func Polym(功能高分子学报) [J],2004,17:607 |
| [9] | Fan L Z,Nan C W,Zhao S J.Solid State Ionics [J],2003,164:81 |
| [10] | Liu Y,Lee J Y,Hong L.J Power Sources [J],2002,109:507 |
| [11] | Wieczorek W,Zalewska A,Siekierski M,et al.Solid State Ionics [J],1996,86:357 |
| [12] | Wieczorek W,Raducha D,Zalewska A,et al.J Phys Chem [J],1998,B102:8 725 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%